7075/6009铝合金层状复合板材的固溶时效热处理工艺
          
Heat Treatment Process for 7075/6009 Aluminum Alloy Laminated Composite Plate

摘    要
对7075/6009铝合金层状复合板材进行了不同的固溶时效处理, 优化得到了该复合板最佳的热处理工艺, 并对热处理后复合板的力学性能和拉伸断口进行了分析。结果表明: 该复合板最佳的热处理工艺为485 ℃×30 min水淬+175 ℃×8 h炉冷, 其抗拉强度为404 MPa, 屈服强度为364 MPa, 伸长率为15.3%; 外层6009铝合金的拉伸断口上分布着大量韧窝, 内外层合金间实现了良好的冶金结合。
标    签 层状复合板材   铝合金   固溶时效   显微组织   力学性能   laminated composite plate   aluminum alloy   solid solution and aging   microstructure   mechanical property  
 
Abstract
Different solid solution and aging treatments were performed with 7075/6009 aluminum alloy laminated composite plate to obtain the optimal heat treatment process, and the mechanical properties and tensile fracture of the composite plate after heat treatment were analyzed. The results show that the optimal heat treatment process of the composite plate was solid solution at 485 ℃ for 30 min followed by water quenching and aging at 175 ℃ for 8 h followed by cooling in furnace. The tensile strength, yield strength and elongation of the composite plate were 404 MPa, 364 MPa and 15.3 %, respectively. A lot of dimples was found on the tensile fracture of outer layer 6009 aluminum alloy and the innerlayer and outerlayer alloys had a good metallurgical bonding.

中图分类号 TG214

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 教育部“新世纪人才支持计划”项目(NCET-07-0310); 广东省科技攻关项目(2008A010300003); 中央高校基本科研业务费资助项目(2009ZM0278)

收稿日期 2011/6/7

修改稿日期 2012/2/8

网络出版日期

作者单位点击查看

备注郑小平(1978-), 男, 广东南雄人, 博士后。

引用该论文: ZHENG Xiao-ping,ZHANG Wei-wen,SHAO Ming,LI Yuan-yuan. Heat Treatment Process for 7075/6009 Aluminum Alloy Laminated Composite Plate[J]. Materials for mechancial engineering, 2012, 36(7): 41~45
郑小平,张卫文,邵明,李元元. 7075/6009铝合金层状复合板材的固溶时效热处理工艺[J]. 机械工程材料, 2012, 36(7): 41~45


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】KIM J K, YU Tong-xi.Forming and failure behaviour of coated, laminated and sandwiched sheet metals a review[J].Journal of Materials Processing Technology, 1997, 63(1/3):33-42.
 
【2】LI Yuan-yuan, ZHANG Wei-wen, CHEN Wei-ping. Preparation and tensile property of a high-strength, anticorrosion functionally graded 2024/3003 composite [J].Journal of Materials Science, 2004, 39(16/17):5607-5609.
 
【3】ZHANG Y X, YANG C H. Recent developments in finite element analysis for laminated composite plates[J].Composite Structures, 2009, 88(1):147-157.
 
【4】GRISHABER R B, SERGUEEVA A V, MISHRA R S, et al.Laminated metal composites-high temperature deformation behavior[J].Materials Science and Engineering A, 2005, 403(1/2):17-24.
 
【5】AYDOGDU M. A new shear deformation theory for laminated composite plates[J].Composite Structures, 2009, 89(1):94-101.
 
【6】YU G. Method for manufacturing gradient material by continuous and semi-continuous casting:United States, 6089309[P].2000-07-18.
 
【7】张卫文, 张大童, 龙雁, 等.高强耐蚀复合铝合金材料:中国, ZL02115163.6[P].2005-06-29.
 
【8】张卫文, 李元元.半连续铸造法制备AlCu/Al梯度材料[J].中国有色金属学报, 2002, 12(增1):188-191.
 
【9】郑小平.梯度复合7075/6009铝合金材料的制备与力学性能研究[D].广州:华南理工大学, 2009.
 
【10】LI Yuan-yuan, ZHENG Xiao-ping, ZHANG Wei-wen, et al.Effect of deformation temperature on microstructures and properties of 7075/6009 alloy[J].Transactions of Nonferrous Metals Society of China, 2009, 19(5):1037-1043.
 
【11】郑小平, 张卫文, 王珺文, 等.内熔体浇口位置对7075/6009合金铸锭内层组织的影响[J].中国有色金属学报, 2009, 19(1):26-31.
 
【12】陈康华, 刘红卫, 刘允中.升温固溶对Al-Zn-Mg-Cu合金组织与力学性能的影响[J].中南工业大学学报, 2000, 31(4):339-341.
 
【13】王祝堂, 田荣章.铝合金及其加工手册[M].长沙:中南大学出版社, 2000.
 
【14】高革.关于飞机用铝合金7075的热处理[J].轻合金加工技术, 1974(4):12-19.
 
【15】陈康华, 刘允中, 刘红卫.7075和2024铝合金的固溶组织与力学性能[J].中国有色金属学报, 2000, 10(6):819-822.
 
【16】曾苏民.影响铝合金固溶保温时间的多因素相关规律[J].中国有色金属学报, 1999, 9(1):79-86.
 
相关信息
   标题 相关频次
 6061铝合金激光填丝焊接接头的组织与力学性能
 6
 冷却工艺对热轧65Mn钢显微组织和力学性能的影响
 6
 冷却速率和碳含量对铁-铜-镍-钼-碳烧结材料组织与性能的影响
 6
 5083/6063不等厚铝合金双丝CMT角焊接头的组织与性能
 5
 固溶升温速率对Al-10.78Zn-2.78Mg-2.59Cu铝合金组织与性能的影响
 5
 挤压工艺参数对4032铝合金组织与性能的影响
 5
 稀土钕对亚共晶铝硅合金组织及性能的影响
 5
 06Cr19Ni10不锈钢/A283低碳钢扩散焊接接头的显微组织和力学性能
 4
 06Cr20Ni11钢埋弧焊焊缝的显微组织和性能
 4
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 4
 12Cr13钢预热处理工艺参数优化
 4
 12Cr1MoV钢过热器爆管的显微组织和力学性能
 4
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 4
 2024铝合金电子束焊接接头的显微组织与力学性能
 4
 240 MPa级高强IF钢的冷轧压下率和退火温度
 4
 300 MW机组锁口叶片断裂原因分析
 4
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 4
 3D打印18Ni300模具钢的显微组织及力学性能
 4
 5 mm厚6005A-T6铝合金双轴肩搅拌摩擦焊接头的组织及性能
 4
 5 mm厚6082-T6铝合金双轴肩搅拌摩擦焊接头的组织与性能
 4
 600 MPa级热轧双相钢的动态连续冷却转变行为及其热轧卷取工艺的优化
 4
 600 MW机组次末级叶片断裂原因分析
 4
 6061-T6铝合金搅拌摩擦焊接头的组织和性能
 4
 6082-T6铝合金搅拌摩擦焊接头的显微组织与力学性能
 4
 7A60-T6超高强铝合金搅拌摩擦焊接头的组织及性能
 4
 960MPa级含钼低碳钢钼含量与热处理工艺的确定
 4
 9Ni钢手工电弧焊和自动埋弧焊接头的组织及力学性能
 4
 A6061-T6铝合金经超声表面纳米化后的显微组织和性能
 4
 Al-1.04Mg-0.85Si-0.01Cu铝合金的热压缩变形行为
 4
 AlNiFeCuCoCrVx高熵合金的显微组织与力学性能
 4