钢基体表面空气助燃超音速火焰喷涂制备铁黄铜涂层的组织和性能
          
Microstructure and Performance of Iron Brass Coating Produced by High Velocity Air-Fuel Spray on Steel Surface

摘    要
采用空气助燃超音速火焰喷涂技术在30CrMnSi钢基体表面上制备出厚3 mm的HFe59-1-1铁黄铜涂层, 对涂层的化学成分、物相组成、显微硬度及耐磨性能进行了研究。结果表明: 制备的铁黄铜涂层呈层状结构, 晶粒细小, 致密度高, 孔隙率小于1%, 和基体结合强度高, 显微硬度为241 HV, 且表现出比同牌号铸造铁黄铜更为优良的耐磨性能。
标    签 空气助燃超音速火焰喷涂   铁黄铜   涂层   耐磨性能   high velocity air-fuel spray(HVAF)   iron brass   coating   wear property  
 
Abstract
Iron brass coating with thickness of 3 mm was prepared on the surface of 30CrMnSi steel substrate by high velocity air-fuel spray. The chemical composition, phase composition, micro-hardness and wear properties of the coating were investigated. The results show that the iron brass coating had layered structure, fine grains, high density, lower porosity of less than 1%, high bonding strength with the substrate and micro-hardness of 241 HV. It had better wear resistance than the as-cast iron brass with same grade.

中图分类号 TG146.1

 
  中国光学期刊网论文下载说明


所属栏目

基金项目

收稿日期 2010/4/19

修改稿日期 2010/12/23

网络出版日期

作者单位点击查看

备注邓畅光(1970-), 男, 广东罗定人, 高级工程师, 硕士。

引用该论文: DENG Chang-guang,DENG Chun-ming,KUANG Min,LIU Min. Microstructure and Performance of Iron Brass Coating Produced by High Velocity Air-Fuel Spray on Steel Surface[J]. Materials for mechancial engineering, 2011, 35(5): 7~10
邓畅光,邓春明,况敏,刘敏. 钢基体表面空气助燃超音速火焰喷涂制备铁黄铜涂层的组织和性能[J]. 机械工程材料, 2011, 35(5): 7~10


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】李长久.超音速火焰喷涂及涂层性能简介[J].表面工程, 1996(4): 29-33.
 
【2】江礼, 王汉功, 侯根良, 等.低温超音速火焰喷涂铜涂层性能研究[J].兵器材料科学与工程, 2005, 28(2): 48-51.
 
【3】周克崧.热喷涂技术替代电镀硬铬的研究进展[J].中国有色金属学报, 2004, 14(1): 182-191.
 
【4】LEGOUX J G, ARSONAULT B, MOREAU C, et al. Evaluation of four high velocity thermal spray gun using WC-10Co-4Cr cermates[C]//Proceedings of the 16th International Thermal Spray Conference. Montreal: ASM International, 2000:479-486.
 
【5】BERGET J, ROGNE T. A summary of recent developments of HVOF sprayed ceramic-metallic coatings for corrosion and wear resistance[C]//Thermal Spray. Ohio: ASM International Materials Park, 2001:1157-1163.
 
【6】申永良, 李维芬.纯铜及其铜合金[J].冶金丛刊, 1998(6): 21-23.
 
【7】王晓峰, 刘德义, 刘世程, 等.钢/黄铜双金属管扩散复合的研究[J].有色金属加工, 2005, 34(1): 27-30.
 
【8】张田仓, 郭德伦.固相连接新技术——搅拌摩擦焊接技术[J].航空工艺技术, 1999(2): 35-37.
 
相关信息
   标题 相关频次
 C/C复合材料高温抗烧蚀涂层的研究进展
 6
 高速火焰喷涂工艺参数对镍基-碳化钨复合涂层结合强度的影响
 6
 近疲劳强度载荷下WC/Co涂层对300M钢疲劳性能的影响
 6
 大气等离子喷涂工艺参数对Cr2O3涂层磨损性能的影响
 5
 空气助燃超音速火焰喷涂WC涂层的性能及应用
 5
 超音速火焰喷涂WC-10Co4Cr涂层的高周疲劳损伤
 4
 铝合金表面活性燃烧高速燃气喷涂WC涂层的耐中性盐雾腐蚀性能
 4
 铜表面激光熔覆镍基合金的显微组织与硬度
 4
 环氧/聚氨脂梯度功能耐磨涂层性能的有限元分析
 3
 以粉煤灰和Al-TiO2-B2O3为原料制备玻璃/陶瓷复合涂层的组织及耐磨性能
 3
 20#钢在三元复合驱弱碱体系采出液中的腐蚀与防护
 2
 FBE与聚苯胺粉末共混涂层的防腐蚀性能
 2
 NiCoCrAlY涂层的抗中性盐雾腐蚀性能
 2
 T91高温过热器管爆裂原因分析
 2
 X射线荧光光谱法测定废塑料表面涂层中8种元素的含量
 2
 ZG06Cr13Ni4Mo不锈钢超音速火焰喷涂WC-10Co-4Cr涂层的抗磨蚀性能
 2
 玻璃纤维和硫脲缓蚀剂对涂层缓蚀行为的影响
 2
 不同表面处理对输电线路铁塔涂层性能的影响
 2
 材料及防护涂层在淡水环境中的腐蚀试验研究
 2
 长庆油田原油储罐腐蚀现状与防腐蚀技术
 2
 长输管线外防护涂层技术的现状与发展探讨
 2
 超声波涂层测厚仪示值误差的不确定度评定
 2
 次高压燃气储罐适用内涂层
 2
 大气等离子喷涂Cr2O3涂层的响应曲面法工艺优化
 2
 大型储罐器壁腐蚀减薄的自动超声扫查
 2
 氮气钻井过程中的耐冲蚀涂层
 2
 等离子喷涂羟基磷灰石涂层残余应力的研究进展
 2
 电弧喷涂铁基非晶纳米晶涂层的耐腐蚀性能
 2
 电弧喷涂铁基镍铬合金涂层的耐碱脆性能
 2
 电化学抛光和阳极氧化处理后TC4钛合金表面的生物活性
 2