500 kV输电线路铁塔塔脚腐蚀原因及处理方案
          
Causes and Treatment Scheme of Tower Foot Corrosion of a 500kV Transmission Tower

摘    要
对某500kV输电线路铁塔塔脚出现严重腐蚀的现场宏观检查,对上底座腐蚀产物取样进行XRD,SEM和EDS分析。结果表明,塔脚的腐蚀是发生在上底座和护板表面的局部腐蚀,主要是大气中SO2对塔脚造成的腐蚀。塔脚所处的位置SO2浓度最高,而锌和A3钢在SO2存在的条件下,腐蚀速率都高于在纯空气中(不含SO2),生成的腐蚀产物结构多孔疏松,且铁塔经常处于潮湿条件下的服役环境能够满足腐蚀持续进行的电化学条件。这些因素共同作用,导致塔脚的腐蚀速率很高,在1~2a的时间内腐蚀减薄已达50%。根据对腐蚀原因的分析,制定了相应的焊补加固和防腐蚀涂料体系方案。
标    签 输电铁塔   腐蚀   腐蚀原因   防腐蚀涂料   transmission tower   corrosion   corrosion cause   anti corrosion coating  
 
Abstract
The causes of severe corrosion of a 500kV transmission tower foot were analyzed and a fix scheme wasformulated.The results of macro inspection,SEM,EDS and XRD analyses of corrosion products sampled from abovepedestal show that the corrosion of tower foot occurring on the pedestal and protective plate surface was localizedcorrosion.The mainly reason was SO2in atmosphere.The position of tower foot had the highest concentration ofSO2.Because of the existence of SO2,the corrosion rate was much higher than that of in the pure air.The structureof corrosion products was porous and service environment was in moist condition,which met the conditions ofelectrochemical corrosion continuous development.These factors worked together and led to a very high corrosion rateof tower foot,the corrosion thinning reached 50% within 1~2a.Thus a welding repair and anticorrosive coatingsystem of corresponding solution was formulated.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 应用技术

基金项目

收稿日期 2013/1/4

修改稿日期

网络出版日期

作者单位点击查看


备注刘爽,工程师,硕士,

引用该论文: LIU Shuang,HU Xin-fang,GAO Sen,FAN Zhi-bin. Causes and Treatment Scheme of Tower Foot Corrosion of a 500kV Transmission Tower[J]. Corrosion & Protection, 2013, 34(11): 1026


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】何长华.输电线路铁塔用钢的发展趋势[J].电力建设,2010,31(1):45-48.
 
【2】陈云,强春媚,王国刚,等. 输电铁塔的腐蚀与防护[J].电力建设,2010,31(8):55-58.
 
【3】Pareja R R,Ibaneg R L,Martin F,et al.Corrosion be-havior of zirconia′s barrier coatings on galvanized steel[J].Surface & Coatings Technology,2006,200:6606-6610.
 
【4】Shibli S M A,Jayalekshmi A C,Remya R.Electro-chemical and structural characterization of the mixedoxides-reinforced hot-dip zinc coating[J].Surface &Coatings Technology,2007,201:7560-7565.
 
【5】Bastos A C,Ferreia M U S,Simoea A M.Comparativeelectrochemical studies of zinc chromate and zinc phos-phate as corrosion inhibitors for zinc[J].Progress inOrganic Coatings,2005,52:339-350.
 
【6】Aramaki K.The inhibition effects of chromate-free,anion inhibitors on corrosion of zinc in aerated 0.5 MNaCl[J].Corrosion Science,2001,43:591-604.
 
【7】梁彩凤,侯文泰.环境因素对钢的大气腐蚀的影响[J].中国腐蚀与防护学报,1998,18(1):1-6.
 
【8】Arroyave C,Lopez F Z,Morcillo M.The early atmos-pheric corrosion stages of carbon steel in acidic fogs[J].Corrosion Science,1995,37(11):1751-1761.
 
相关信息
   标题 相关频次
 锅炉水冷壁管内壁腐蚀泄漏原因分析及处理
 6
 输电线路铁塔腐蚀等级评定规则
 5
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 10号碳钢在NaOH溶液中的腐蚀电化学行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 20号钢在气田站场分离器积液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304H弹簧钢丝及弹簧表面腐蚀的原因
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2
 304不锈钢在高温环烷酸介质中的腐蚀行为
 2
 30CrMnSiA合金钢当量加速腐蚀试验
 2
 316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为
 2
 316L不锈钢在有机胺脱硫溶液中的耐蚀性
 2
 445铁素体不锈钢内胆水箱的加工性能和耐蚀性
 2
 45号钢在硫化氢水溶液中的腐蚀行为
 2
 5083铝壳艇外加电流阴极保护系统研制
 2
 7A04和2A12铝合金在吐鲁番干热大气环境中的腐蚀行为
 2
 9S75铝合金的电化学腐蚀行为及阳极氧化工艺
 2
 A3钢在海泥中的腐蚀行为
 2