45号钢在硫化氢水溶液中的腐蚀行为
          
Corrosion Behavior of 45#Steel in Hydrogen Sulfide Solutions

摘    要
为了解硫化氢对金属材料造成的腐蚀和氢脆的影响,探索硫化氢的腐蚀机理,将45号钢在不同浓度H2S溶液、不同时间浸泡后,采用硬度试验的方法,对材料的硬度变化情况、腐蚀层厚度、渗透层厚度以及氢脆影响层厚度的变化情况进行了研究。结果表明,45号钢经受H2S腐蚀后的硬度会随着材料的层深而呈现先上升、后下降直至恢复到原始硬度的趋势;H2S溶液浸泡对中碳钢产生了腐蚀和氢脆两种影响,材料经48h浸泡后受到H2S氢脆效应的影响最显著,经96h浸泡后受到的腐蚀影响最显著。
标    签 H2S溶液   腐蚀   氢脆   硬度   H2S solution   corrosion   hydrogen embrittlement   hardness  
 
Abstract
In order to study the influence of hydrogen sulfide on corrosion and hydrogen embrittlement and to explorethe corrosion mechanism in hydrogen sulfide environments,45#steel was immersed in solutions containing differentconcentrations of H2S for various hours.The changes of the hardness,the thickness of the corroded layer,thethickness of the permeation layer and the thickness of the layer affected by hydrogen embrittlement were studied.Theresults show that the hardness of the specimen first increased and then decreased until it was restored to the originalhardness after the material subjected to the corrosion of hydrogen sulfide.Solution containing H2S can induce twoeffects of corrosion and hydrogen embrittlement.It was found that the effect of the H2S hydrogen embrittlement wasthe most significant after 48himmersion,and the effect of the corrosion was the most significant after 96 himmersion.

中图分类号 TG174.3+1 O341 TG115.5+1

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2013/1/7

修改稿日期

网络出版日期

作者单位点击查看


备注翟建明,博士研究生,

引用该论文: ZHAI Jian-ming,LI Xiao-yang,WU Ming-yao,ZHANG Yi-liang. Corrosion Behavior of 45#Steel in Hydrogen Sulfide Solutions[J]. Corrosion & Protection, 2013, 34(11): 1013


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】陈明,崔琦.硫化氢腐蚀机理和防护的研究现状及进展[J].石油工程建设,2010,36(5):1-5.
 
【2】张亦良,徐金泉,王羽辞.石化特种设备中的硫化氢应力腐蚀与残余应力[J].中国工程科学,2009(8):38-43.
 
【3】刘智勇,李明,李晓刚.16Mn(HIC)钢在硫化氢环境中的应力腐蚀开裂行为[J]. 中国腐蚀与防护学报, 2006,26(6):360-364.
 
【4】Rogante A,Battistella P,Cesari F.Hydrogen interac-tion and stress-corrosion in hydrocarbon storage vesseland pipeline weldings[J].Int J Hydrogen Energ,2006,31(5):597-601.
 
【5】任学冲,褚武扬,李金许,等.夹杂对氢鼓泡形成的影响[J].金属学报,2007,43(7):673-677.
 
【6】李云涛,杜则裕,孙娈芬,等.高强度管线钢的抗氢致裂纹性能[J].钢铁研究学报,2008,20(12):50-54.
 
【7】顾宝兰,徐学东,周莉.管线用钢显微组织对氢致裂纹影响的研究[J].理化检验-物理分册,2006,42(1):8-11.
 
【8】Zinbi A,Bouchou A.Delayed cracking in 301austeniticsteel after bending process:Martensitic transformationand hydrogen embrittlement analysis[J].Eng Fail A-nal,2010,17(5):1028-1037.
 
【9】鲁连涛,盐泽和章,森井佑一,等.高碳铬轴承钢超长寿命疲劳破坏过程的研究[J]. 金属学报, 2005,41(10):1066-1072.
 
【10】赵颖,王荣.X70管线钢电化学充氢后的力学行为研究[J].中国腐蚀与防护学报,2004,24(5):293-296.
 
【11】李会录,余竹焕,李颖,等.高强钢氢脆敏感性和氢致附加应力的相关性[J].腐蚀与防护,2009,30(10):678-683.
 
【12】Marcelo A L,Tokimatsu R C,Ferreira I.Hydrogenembrittlement in an AISI 1045steel component of thesugarcane industry[J].Eng Fail Anal,2009,16(1):468-474.
 
【13】寇杰,梁法春,陈婧.油气管道腐蚀与防护[M].北京:中国石化出版社,2008.
 
【14】肖纪美.应力作用下的金属腐蚀 应力腐蚀、氢致开裂、腐蚀疲劳、磨耗腐蚀[M].北京:化学工业出版社,1990.
 
【15】Swieczko-Zurek B,Zielinski A,Lunarska E.Hydro-gen degradation of structural steels in technical hy-drocarbon liquids[J].Mater Corros,2008,59(4):289-295.
 
【16】李志林,陈涛,曾致翚.不锈钢电化学诱导退火过程中的氢及其扩散系数测定[J].北京化工大学学报:自然科学版,2005,32(5): 60-63.
 
相关信息
   标题 相关频次
 1018钢螺钉断裂失效分析
 4
 超声波作用下电沉积纳米晶Co-W合金镀层
 4
 高强度螺栓断裂原因分析
 4
 钛铜共用海水冷却器的牺牲阳极保护
 4
 天然气管道开裂的原因
 4
 常压储罐罐底腐蚀的漏磁检测与失效分析
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 102钢的显微组织形态与室温力学性能的关系
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 10Cr9Mo1VNbN钢大直径三通锻件的硬度规定值取值分析
 2
 12.9级内六角圆柱螺栓断裂失效分析
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 13Cr钢防砂工具转换接头开裂原因分析
 2
 13MnNiMoNbR与00Cr19Ni10异种钢焊接接头的组织与性能
 2
 16MND5/309L/308L/Z2CND18-12N异种金属焊接件的组织和性能
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2
 304不锈钢低温分离器开裂原因分析
 2
 304不锈钢在高温环烷酸介质中的腐蚀行为
 2
 30CrMnSiA合金钢当量加速腐蚀试验
 2