FBE与聚苯胺粉末共混涂层的防腐蚀性能
          
Anti-corrosion Performance of FBE Coatings with Addition of Polyaniline Powders

郭英   陈飞  
摘    要
以苯胺为单体, 过硫酸铵为氧化剂, 采用超声波辅助的化学氧化法合成了聚苯胺, 自制的聚苯胺与熔结环氧粉末(FBE)混合均匀后, 用静电喷涂法在Q235钢上制备涂层。采用电化学阻抗谱(EIS)技术研究涂层在模拟海水中不同浸泡时期的防腐蚀性能。结果表明, 聚苯胺粉末的加入提高了FBE涂层的防腐蚀性能, 且加入量较少时, 涂层的耐腐蚀性能随着聚苯胺含量的增加而增强, 当质量分数达到5%时效果最好; 在达到10%后, 涂层中没有足够的粘结剂来填充聚苯胺之间的空间, 使涂层多孔, 防腐蚀性能变差。
标    签 熔结环氧粉末(FBE)   聚苯胺   涂层   电化学阻抗谱(EIS)   fusion bonded epoxy(FBE)   polyaniline   coating   EIS  
 
Abstract
Polyaniline composites were prepared by ultrasonic assisted chemical oxidation method, with aniline as monomer and ammonium persulfate as oxidizing agent. After the composites were mixed with fusion bonded epoxy(FBE), a compound coating was prepared on Q235 steel surface by electric spraying technology. The anti-corrosion performance of the coating in simulated seawater solution for different immersion durations was studied by EIS. The results indicate that the anti-corrosion performance of the FBE coating was strengthened with increasing the content of polyaniline when the added content of polyaniline was relatively low. The best performance was obtained when the content of polyaniline was 5%, but the anti-corrosion performance became worse when the content of polyaniline was 10% because the coating was not adhesive enough to fill the space between the polyaniline powders.

中图分类号 TG174.46

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2011/9/21

修改稿日期

网络出版日期

作者单位点击查看

联系人作者郭英(gy310@163.com)

备注郭英, 教授,

引用该论文: GUO Ying,CHEN Fei. Anti-corrosion Performance of FBE Coatings with Addition of Polyaniline Powders[J]. Corrosion & Protection, 2012, 33(8): 683


被引情况:


【1】徐健,林栋, "纳米自修复涂层在GH907材料腐蚀防护上的应用",腐蚀与防护 35, 1144-1147(2014)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】毕学振. 熔结环氧粉末涂料的应用与施工介绍[J]. 中国涂料, 2006, 2(12):43-45.
 
【2】DeBerry W. Modification of the electrochemical and corrosion behavior of stainless steel with an electroactive coating[J]. Electrochemical Society, 1985, 132(5):1022-1026.
 
【3】刘军喜, 苏光耀, 高德淑, 等. 聚苯胺防腐涂料的制备与性能研究[J]. 表面技术, 2005, 34(1):50-52.
 
【4】张清华, 王献红, 景遐斌. 聚苯胺的合成及光谱特征[J]. 化学世界, 2001, 5:242-244.
 
【5】张鉴清, 曹楚南. 电化学阻抗谱方法研究评价有机涂层[J]. 腐蚀与防护, 1998, 19(3):99-104.
 
【6】吴剑锋, 王结良, 吕涛, 等. 电化学阻抗谱研究三种涂层体系的耐蚀性[J]. 腐蚀与防护, 2010, 31(10):760-762.
 
【7】王建雄, 郭清萍, 郭有军. 聚苯胺防腐蚀涂料的研究现状[J]. 腐蚀与防护, 2008, 28(4):211-215.
 
【8】Sathiyanarayanan S, Muthkrishnan S, Venkatachari G. Corrosion protection of steel by polyaniline blended coating[J]. Electrochimica Acta, 2006, 51(28):6313-6319.
 
【9】Sathiyanarayanan S, Muthukrishnan S, Venkatachari G. Performance of polyaniline pigmented vinyl acrylic coating on steel in aqueous solutions[J]. Progress in Organic Coatings, 2006, 55(1):5-10.
 
【10】Kinlen P J, Silverman D C, Jeffreys C R. Corrosion protection using polyaniline coating formulations[J]. Synthetic Metals, 1997, 101(1/3):1327-1332.
 
【11】涂料工艺编委会. 涂料工艺(第三版)下册[M]. 北京:化学工业出版社, 1997:360-362.
 
【12】潘莹, 张三平, 周建龙, 等. 有机涂层的屏蔽作用及其影响因素[J]. 腐蚀与防护, 2010, 31(9):741-744.
 
【13】高焕方, 张胜涛, 彭超, 等. 聚苯胺丙烯酸涂层的防腐蚀性能[J]. 腐蚀与防护, 2010, 31(5):353-354.
 
相关信息
   标题 相关频次
 掺杂态聚苯胺的合成及其在碳钢/HCl体系中的复合缓蚀行为
 5
 不同表面处理对输电线路铁塔涂层性能的影响
 4
 20#钢在三元复合驱弱碱体系采出液中的腐蚀与防护
 3
 玻璃纤维和硫脲缓蚀剂对涂层缓蚀行为的影响
 3
 二次掺杂聚苯胺的防腐蚀性能
 3
 聚苯胺丙烯酸涂层的防腐蚀性能
 3
 聚苯胺对环氧涂层防腐蚀性能的影响
 3
 两种硅钢丙烯酸树脂涂层的电化学阻抗性能比较
 3
 2-(4-吡啶基)苯并咪唑对碳钢的缓蚀行为
 2
 20CrNiMo钢表面磁控溅射制备TiN/ZrN多层薄膜的形貌及摩擦学性能
 2
 20钢多元共渗后的耐腐蚀性能
 2
 40Cr钢表面低温气体碳、氮、氧多元共渗层的摩擦学性能
 2
 C/C复合材料高温抗烧蚀涂层的研究进展
 2
 HTPB推进剂温度冲击环境下损伤特性的声发射试验
 2
 P/B对水性聚氨酯防腐蚀涂料性能影响研究
 2
 X70钢在卵石黄泥土中的盐浓差宏电池腐蚀
 2
 X射线荧光光谱法测定废塑料表面涂层中8种元素的含量
 2
 ZG06Cr13Ni4Mo不锈钢超音速火焰喷涂WC-10Co-4Cr涂层的抗磨蚀性能
 2
 丙炔醇对Q235钢在硫酸中的缓蚀作用
 2
 不同时效状态新型Al-Cu-Li系合金腐蚀的电化学阻抗谱
 2
 不同质子酸二次掺杂聚苯胺的导电性能
 2
 材料及防护涂层在淡水环境中的腐蚀试验研究
 2
 掺杂纳米钛导静电涂层的耐蚀性能
 2
 掺杂态和本征态聚苯胺对不锈钢的保护作用
 2
 长庆油田原油储罐腐蚀现状与防腐蚀技术
 2
 长输管线外防护涂层技术的现状与发展探讨
 2
 超声波涂层测厚仪示值误差的不确定度评定
 2
 次高压燃气储罐适用内涂层
 2
 大型储罐器壁腐蚀减薄的自动超声扫查
 2
 氮气钻井过程中的耐冲蚀涂层
 2