7A04和2A12铝合金在吐鲁番干热大气环境中的腐蚀行为
          
Corrosion Behavior of 7A04 and 2A12 Aluminum Alloys in Hot and Dry Atmosphere Environment in Turpan

摘    要
采用现场暴晒试验,研究了7A04和2A12两种铝合金在吐鲁番干热大气环境中的腐蚀行为和机理。1 a暴露后的失重分析发现7A04的腐蚀速率大于2A12; 采用SEM和EDS观察分析了两种合金表面的腐蚀产物,结果表明,均主要由铝的氧化物和氢氧化物组成。去除腐蚀产物后, 7A04表面呈现大量密集腐蚀坑,而2A12表面腐蚀坑则较少。EIS结果表明,两种合金的腐蚀产物层电阻电容差别较大,带腐蚀产物2A12的耐蚀性优于7A04。
标    签 铝合金   吐鲁番   干热大气   腐蚀   aluminum   Turpan   hot and dry atmosphere environment   corrosion  
 
Abstract
The corrosion behavior and mechanism of 7A04 and 2A12 aluminum alloys exposed for 1 year in the hot and dry atmosphere environment in Turpan were studied. The results of weight lose tests showed that the corrosion rate of 7A04 aluminum alloy was greater than that of 2A12. The results of scanning electron microscopy(SEM) and energy dispersive spectra showed that the corrosion products on the surface of the aluminum alloys were composed of aluminum oxides and hydroxides. After removal of corrosion products, the number of corrosion pits on 7A04 aluminum alloy was more than that on 2A12. The results of electrochemical impedance spectroscopy showed that the resistance and capacitance of corrosion product layer had large difference between the two kinds of aluminum alloys, 2A12 aluminum alloy with corrosion products had better corrosion resistance than 7A04 aluminum alloy.

中图分类号 TG172.3

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家材料环境腐蚀平台(2005DKA10400); 吐鲁番干热大气环境材料腐蚀试验研究平台建设(PT1207)

收稿日期 2013/12/18

修改稿日期

网络出版日期

作者单位点击查看


备注李慧艳(1987-),博士研究生,从事金属腐蚀与防护工作,

引用该论文: LI Hui-yan,FANG Yue-hua,XIAO Kui,GUO Chun-yun,DONG Chao-fang,LI Xiao-gang. Corrosion Behavior of 7A04 and 2A12 Aluminum Alloys in Hot and Dry Atmosphere Environment in Turpan[J]. Corrosion & Protection, 2014, 35(11): 1098


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】SMITH B J,WARKE P A,MCGREEVY J P,et al. Salt-weathering simulations under hot desert conditions: agents of enlightenment or perpetuators of preconceptions[J]. Geomorphology,2005,67:211-227.
 
【2】李慧艳,方月华,肖葵,等. 干热大气环境中涂层材料失效行为研究进展[J]. 科技导报,2012,30(34):76-79.
 
【3】NING A L,LIU Z Y,ZENG S M. Effect of large cold deformation after solution treatment on precipitation characteristic and deformation strengthening of 2024 and 7A04 aluminum alloys[J]. Transactions of Nonferrous Metals Society of China,2006,16:1341-1347.
 
【4】DONG C F,SHENG H,AN Y H,et al. Corrosion of 7A04 aluminum alloy under defected epoxy coating studied by localized electrochemical impedance spectroscopy[J]. Progress in Organic Coatings,2010,67:269-273.
 
【5】WANG B,ZHANG L W,SU Y,et al. Investigation on the corrosion behavior of aluminum alloys 3A21 and 7A09 in chloride aqueous solution[J]. Materials & Design,2013,50:15-21.
 
【6】周和荣,李晓刚,董超芳,等. 7A04铝合金在薄液膜下的腐蚀行为[J]. 北京科技大学学报,2008,30(8):880-887.
 
【7】ZHOU H R,LI X G,DONG C F,et al. Corrosion behavior of aluminum alloys in Na2SO4 solution using the scanning electrochemical microscopy technique[J]. International Journal of Minerals,16(1):84-88.
 
【8】李涛,吴立凡,李相前,等. Cl-浓度对2A12铝合金电化学行为的影响[J]. 腐蚀与防护,2011,32(4):256-296.
 
【9】郑弃非,孙霜青,温军国. 铝及铝合金在我国的大气腐蚀及其影响因素分析[J]. 腐蚀与防护,2009,30(6):359-419.
 
相关信息
   标题 相关频次
 pH值对2024-T351铝合金在NaCl溶液中电化学行为的影响
 6
 不同NaCl浓度对耐候钢腐蚀产物的影响
 6
 大气腐蚀中液滴覆盖下腐蚀现象的研究方法进展
 6
 金属腐蚀微区电化学研究进展(1)扫描电化学显微镜技术
 6
 金属腐蚀微区电化学研究进展(2)局部电化学阻抗谱
 6
 金属腐蚀微区电化学研究进展(3)扫描振动电极技术
 6
 离子交换型缓蚀填料在防腐蚀涂层中的应用Ⅰ阳离子交换型填料
 6
 离子交换型缓蚀填料在防腐蚀涂层中的应用Ⅱ 阴离子交换型填料
 6
 三种典型接地极材料在陕北土壤模拟溶液中的腐蚀行为
 6
 三种电弧喷涂涂层在大庆地区土壤中的腐蚀性
 6
 三种电弧喷锌防护涂层在3.5% NaCl溶液中的耐蚀性
 6
 水溶性壳聚糖对双相不锈钢的缓蚀作用
 6
 环境因素对铝合金大气腐蚀的影响及其强激光与粒子束动态变化规律研究
 5
 铝合金表面溶胶-凝胶防腐蚀膜层研究进展及展望
 5
 316L不锈钢、690合金在氢氧化钠溶液中的电化学性能
 4
 7A04铝合金在西沙海洋大气中的腐蚀行为
 4
 高温环烷酸腐蚀机理与控制方法研究进展
 4
 硫酸溶液中Fe3+对TC4腐蚀行为的影响
 4
 酸性土壤中的模拟滞留液溶液对X80钢腐蚀行为的影响
 4
 阵列电极(WBE)联合线性极化技术(LP)研究海水-大气界面区碳钢的腐蚀行为
 4
 2A12铝合金当量加速腐蚀试验
 3
 9S75铝合金的电化学腐蚀行为及阳极氧化工艺
 3
 等离子电解氧化脉冲电压对铝合金陶瓷层结构的影响
 3
 高耐蚀性铬酸阳极氧化工艺研究
 3
 基于元胞自动机法的铝合金腐蚀行为模拟
 3
 近海含SO2环境中高压隔离开关铝合金部件的组织及腐蚀特征
 3
 利用声发射技术检测储罐的腐蚀损伤状态
 3
 微弧氧化铝合金在海水中的腐蚀行为
 3
 沿海工业环境下6A02铝合金接线板的腐蚀行为
 3
 荧光分析法检测Cl-溶液中AA6061铝合金的腐蚀
 3