6061铝合金表面氟钛酸盐转化新工艺
          
A Novel Fluorine-titanate Conversion Process on 6061 Aluminum Alloy Surface

摘    要
以6061铝合金为基体, 在由钛盐和氟化钠组成的转化液中制得无铬转化膜。以盐雾试验后试样未腐蚀面积为指标, 采用正交试验研究了转化液的组成和工艺条件对氟钛酸盐转化膜耐蚀性的影响。优化后氟钛酸盐转化工艺参数为: 钛盐1.5 g/L, 氟化钠3 g/L, H2O2 1.5 mL/L, 转化时间10 min, 处理液pH=5.0。
标    签 6061铝合金   工艺优化   氟钛酸盐转化膜   耐蚀性   6061 aluminum alloy   process optimization   fluorine-titanate conversion coating   corrosion resistance  
 
Abstract
A chromium-free conversion coating on 6061 aluminum substrate was prepared from a conversion solution containing titanate and sodium fluoride. The uncorroded area fraction of the sample after salt spray test was served as the index to study the effect of the composition of conversion solution and process parameters on the corrosion resistance of conversion coating. The optimized process parameters of fluorine-titanate conversion are as follow: titanium salt 1.5 g/L, sodium fluoride 3 g/L, hydrogen peroxide1.5 mL/L, normal temperature, pH=5.0, and conversion time 10 min.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 应用技术

基金项目 河南省科技攻关重点项目(122102310321); 商丘市科技攻关项目(141003)

收稿日期 2014/4/22

修改稿日期

网络出版日期

作者单位点击查看


备注李红玲(1977-),讲师,硕士,从事金属材料表面改性方面的研究,

引用该论文: QIN Zhen-Hua,LI Hong-ling. A Novel Fluorine-titanate Conversion Process on 6061 Aluminum Alloy Surface[J]. Corrosion & Protection, 2014, 35(7): 742


被引情况:


【1】李红玲,刘双枝, "6061铝合金氟钛酸盐转化膜耐蚀性能的改性研究",腐蚀与防护 36, 938-941(2015)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】龚伟慧, 陈东初, 李文芳,等. 环境友好型铝合金化学转化表面处理技术的发展概况[J]. 材料研究与应用, 2009, 3(1):1-4.
 
【2】HINTON B R W. Corrosion prevention and chromates:The End of an Era[J]. Metal Finishing, 1991, 89(9):55-58.
 
【3】韩哲, 熊金平, 左禹. 铝合金表面化学氧化工艺的研究进展[J]. 电镀与精饰, 2008, 30(11): 14-18.
 
【4】郭瑞光, 杨杰, 康娟. 铝合金表面钛酸盐化学氧化膜研究[J]. 电镀与涂饰, 2006, 25(1): 46-48.
 
【5】NORDLIEN J H, WALMSLEY J C, NISANCIOGLU K, et al. Formation of a zirconium-titanium based conversion layer on AA6060 aluminium[J]. Surface and Coatings Technology, 2002, 153(1): 72-78.
 
【6】LUNDER O, SIMENSEN C, YU Y, et al. Formation and characterisation of Ti-Zr based conversion layers on AA6060 aluminum[J]. Surface and Coatings Technology, 2004, 184(2/3): 278-290.
 
【7】王娜娜, 郭瑞光, 唐长斌, 等. 2024 铝合金氟铝酸盐转化膜的制备及其防腐蚀性能[J]. 材料保护, 2012, 45(5): 38-41.
 
【8】郭瑞光,王晓昌,耿志良,等. 环境友好型铝合金表面转化膜的制备及其耐蚀性能[J]. 材料保护, 2008, 41(12): 14-16.
 
【9】白锐, 丁晓莉, 肖雄,等. 一种新型环保铝合金无铬钝化处理液[J]. 广东化工, 2012, 39(6): 127-128.
 
【10】陈东初,黄柱周,李文芳. 铝合金表面无铬化学转化膜的研究[J]. 表面技术,2005,34(6):38-39.
 
【11】ANDREATTA F,TURCO A,GRAEVEL D,et al. SKPFM and SEM study of the deposition mechanism of Zr/Ti based pre-treatment on AA6016 aluminum alloy[J]. Surface & Coatings Teclmology,2007,201:7668-7685.
 
【12】LAHA P,SEHRAM T,TERRYN H. Use of spectroscopic elliPsometry to study Zr/Ti films on Al[J]. Surf Interface Anal,2002,34:677-680.
 
相关信息
   标题 相关频次
 6061铝合金氟钛酸盐转化膜耐蚀性能的改性研究
 6
 6061铝合金镧转化膜工艺参数的正交优化
 6
 常温铁系磷化工艺研究
 4
 超细晶AZ91D镁合金表面的微弧氧化工艺优化
 4
 焊接对00Cr22Ni5Mo3N筒体耐蚀性的影响及工艺优化
 4
 汽车用6061铝合金板的搅拌摩擦加工改性
 3
 201不锈钢表面弧光离子镀TiN和CrN薄膜的耐蚀性
 2
 20钢多元共渗后的耐腐蚀性能
 2
 2205双相不锈钢在硫酸中的腐蚀性能
 2
 2205与15MnNiCrMoV异质钢焊接接头的耐蚀性能
 2
 304不锈钢表面锈蚀原因分析
 2
 316L与2205不锈钢的腐蚀行为研究现状
 2
 3mm厚6061铝合金板固定双轴肩搅拌摩擦焊接头的显微组织与拉伸性能
 2
 6061铝合金上硅烷膜的制备与性能
 2
 6061铝合金在多向锻造过程中显微组织与拉伸性能的演变
 2
 65Mn、35Cr2Ni3MoV和AF1410在模拟海洋环境中的耐蚀性
 2
 7A04-T6铝合金中金属间化合物对其阳极氧化膜耐蚀性的影响
 2
 A356铝合金车轮T6热处理工艺的优化
 2
 AA5052铝合金表面化学镀锡及其耐蚀性
 2
 AM60压铸镁合金表面微弧氧化陶瓷层的耐蚀性电化学分析
 2
 AZ40M镁合金锻件不规则形状缺陷分析
 2
 AZ91D镁合金Ni-P/CeO2化学复合镀层的耐蚀性
 2
 AZ91D镁合金表面化学镀Ni-P-SiC复合镀层的结构与性能
 2
 AZ91D镁合金电弧喷涂铝锌工艺的研究
 2
 AZ91D镁合金微弧氧化膜厚对其耐蚀性的影响
 2
 AZ91镁合金表面电化学沉积羟基磷灰石涂层的制备及其耐蚀性
 2
 CMOS探测器在射线检测中的应用
 2
 Fe、Cr过饱和固溶量对Zr-4合金耐蚀性的影响
 2
 HAl77-2铜合金管在低温多效海水淡化装置中的耐蚀性
 2
 KIO3对铝合金化学沉积Ni-P镀层的影响
 2