AZ31镁合金表面沉积类金刚石薄膜在Hank′s体液中的腐蚀行为
          
Corrosion Behavior of Diamond-like Carbon Film on Magnesium Alloy in Hank′s Body Fluid

摘    要
采用电化学方法测试了镀类金刚石薄膜镁合金试样在模拟体液中的腐蚀行为、极化曲线和开路电位, 结果表明, 试样在模拟体液中极化行为与AZ31镁合金在模拟体液中相似。采用扫描电镜观测了腐蚀24 h后试样的形貌, 采用失重法和集氢气法测试了试样在模拟体液中腐蚀速率和析氢量随时间变化情况, 结果表明, 镀有类金刚石薄膜的镁合金比AZ31镁合金具有更好的耐蚀性。
标    签 镁合金   类金刚石薄膜   人体植入材料   腐蚀   体液   magnesium alloy   diamond-like carbon film   human body implant material   corrosion   body fluid  
 
Abstract
The corrosion behavior of diamond-like carbon film on magnesium alloy in Hank′s simulated body fluid was investigated. The polarization curve and open circuit potential of diamond-like carbon film on magnesium alloy were evaluated by electrochemical methods. It was found that the polarization behavior of diamond-like carbon film on magnesium alloy in simulated body fluid was similar to that of AZ31 magnesium alloy. The corrosion morphology was observed by SEM. The corrosion rate of the samples and hydrogen evolution as a function of in simulated body fluid were tested by weight loss method and hydrogen collection method. The results showed that diamond-like carbon film on magnesium alloy had better corrosion resistance than AZ31 magnesium alloy.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2013/9/13

修改稿日期

网络出版日期

作者单位点击查看


备注吴楠(1987-),硕士,从事镁合金腐蚀与防护,

引用该论文: WU Nan,ZHAO Hong-yang,GU Ting-ting. Corrosion Behavior of Diamond-like Carbon Film on Magnesium Alloy in Hank′s Body Fluid[J]. Corrosion & Protection, 2014, 35(7): 725


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】黄晓梅, 王艳艳, 刘飒. 镁锂合金在模拟人体体液中的腐蚀[J]. 腐蚀与防护, 2011,32(10):785-787.
 
【2】宋光玲, 宋诗哲. 镁在人体模拟液中的腐蚀行为[J]. 物理化学学报, 2006,22(10): 1222-1226.
 
【3】洪岩松,杨柯,张广道,等. 可降解镁合金的动物体内骨诱导作用[J]. 金属学报, 2008,44(9):1035-1041.
 
【4】HAFERKAMP H,BOEHM R,HOLZKAMP U,et al. Alloy development,processing and applications in magnesium lithium alloys[J]. Materials Transactions,2001,42(7):1160-1166.
 
【5】GUO Y Y,ZHAO H Y,JU D Y,et al. Structure and electrochemical properties of DLC/SiC films on the surface of magnesium alloy by plasma immersion ion deposition[J]. Material Science Forum,2013,750:298-301.
 
【6】JONE S M I,MCCOLL I R,GRANT D M. Protein adsorption and platelet attachment and activation on TiN,TiC and DLC coatings on titanium for cardiovascular applications[J]. Biomedical Matererial Research,2000,52:413-421.
 
【7】JIANG S W,YIN G F,ZHENG C Q. An investigation of the biotribological performance of DLC film-Ti6Al4V gradient material and its effect on hemocompatibility[C]//Shanghai:Proceeding of 12th Interdisciplinary Research Conference on Biomaterials,2002:155.
 
【8】宋光玲. 镁合金的腐蚀与防护[M]. 北京: 化学工业出版社, 2006.
 
【9】CHIU K Y,WONG M H,WONG F T. Characterization and corrosion studies of fluoride conversion coating on degradable Mg implants[J]. Surface and Coating Technology ,2007,202:590-598.
 
【10】吴茂江. 硅与人体健康[J]. 微量元素与健康研究,2012,29(128):65-67.
 
相关信息
   标题 相关频次
 AZ31镁合金的阳极氧化新工艺
 4
 Sr对AZ31B镁合金微观组织和腐蚀性能的影响
 4
 含稀土耐蚀Mg-9Al铸造镁合金腐蚀行为研究
 4
 镁合金的腐蚀与防护研究进展
 4
 镁合金腐蚀的影响因素
 4
 硝酸铈对镁合金在硝酸铵溶液中的缓蚀作用
 4
 一种AZ80铸造镁合金用高效微弧氧化工艺
 4
 一种新的AZ40镁合金阳极氧化工艺
 4
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 10号碳钢在NaOH溶液中的腐蚀电化学行为
 2
 12Cr-F/M钢在超临界水中的腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 2
 1Cr11Ni2W2MoV不锈钢冲击性能不合格原因探讨
 2
 201型不锈钢在酸性食物模拟环境中的腐蚀行为
 2
 20G/316L双金属复合管失效的原因
 2
 20号钢在HCl-H2S-H2O溶液中的腐蚀行为
 2
 20号钢在气田站场分离器积液中的腐蚀行为
 2
 220kV钢芯铝绞线断股事故化学分析
 2
 2507双相不锈钢钾盐蒸发罐腐蚀的原因分析
 2
 2A12铝合金当量加速腐蚀试验
 2
 2-甲基咪唑啉及其复配缓蚀剂在高硬度电解质水溶液中的缓蚀性能
 2
 304H弹簧钢丝及弹簧表面腐蚀的原因
 2
 304L不锈钢焊接接头表面状态对其在硼酸溶液中腐蚀行为的影响
 2
 304不锈钢在高温环烷酸介质中的腐蚀行为
 2
 30CrMnSiA合金钢当量加速腐蚀试验
 2
 316L不锈钢在熔融LiCl-3%Li2O中的腐蚀行为
 2