12Cr-F/M钢在超临界水中的腐蚀行为
          
Corrosion Behavior of 12Cr-F/M Steel in Supercritical Water

摘    要
采用慢应变速率试验(SSRT)研究了12Cr-F/M钢在25 MPa,550 ℃和650 ℃的超临界水(SCW)中的机械性能,以及在550 ℃的SCW中的应力腐蚀开裂(SCC)倾向。同时通过均匀腐蚀试验研究了12Cr-F/M钢在550 ℃/25 MPa的SCW中的腐蚀性能。SSRT结果表明,12Cr-F/M钢在550 ℃/25 MPa时具有优良的机械性能,当温度升高到650 ℃时其机械强度下降明显,但延伸率基本不变。由断口SEM形貌可知,12Cr-F/M钢具有沿晶应力腐蚀开裂(IGSCC)倾向。均匀腐蚀结果表明,12Cr-F/M钢在550 ℃/25 MPa的SCW中的腐蚀性能较差,其腐蚀增重呈现出抛物线生长规律,1 000 h后其腐蚀增重达741 mg/dm2。同时发现其在600 h时表面氧化膜出现裂纹,1 000 h时后观察到氧化膜发生剥落,而氧化膜脱落主要是因为在降温过程中基体与氧化物间不一致的热膨胀系数造成的。
标    签 腐蚀   应力腐蚀开裂   机械性能   超临界水   corrosion   SCC   mechanical performance   supercritical water (SCW)  
 
Abstract
The mechanical properties of 12Cr-F/M steel at 550/650 ℃ and SCC performance at 550 ℃ in supercritical water (SCW) were studied using slow strain rate testing (SSRT). And the general corrosion behavior of 12Cr-F/M steel in SCW at 550 ℃ was studied. The results of SSRT showed that 12Cr-F/M steel had good mechanical properties in SCW at 550 ℃, and its mechanical strength decreased significantly when the temperature was 650 ℃, but its elongation was basically unchanged. The result of ex-situ scanning electron microscopy (SEM) showed that 12Cr-F/M steel had IGSCC susceptibility in SCW at 550 ℃. The result of general corrosion experiment in supercritical water showed that 12Cr-F/M steel had low resistance to general corrosion, and the weight gain was subject to Parabolic growth law. At 600 h, the rupture of oxide film occurred, and the oxide film suffered exfoliation at 1 000 h. It is assumed that this exfoliation resulted from the inconsistency of thermal expansion between the matrix and the oxide during the cooling period.

中图分类号 TG174

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 大型先进压水堆核电站重大专项(2011ZX06004010)

收稿日期 2013/7/5

修改稿日期

网络出版日期

作者单位点击查看


备注张乐福(1967-),副教授,博士后,从事材料研究,

引用该论文: SHEN Zhao,DUAN Zhen-gang,SUN Yao,ZHANG Le-fu,XU Xue-lian. Corrosion Behavior of 12Cr-F/M Steel in Supercritical Water[J]. Corrosion & Protection, 2014, 35(5): 434


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】PETER KRITZER. Corrosion in high-temperature and supercritical water and aqueous solutions:a review[J]. Journal of Supercritical Fluids,2004,29.
 
【2】CHEN Y,KUMAR Sridharan,TODD Allen. Corrosion behavior of ferritic-martensitic steel T91 in supercritical water[J]. Corrosion Science,2006(48):2843-2854.
 
【3】CHEN Y,KUMAR Sridharan,TODD R,et al. Microstru-ctural examination of oxide layers formed on an oxide dispersion strengthened ferritic steel exposed to supercritical water[J]. Journal of Nuclear Materials,2006(359):50-58.
 
【4】GUPTA G,AMPORNRAT P,REN X,et al. Role of grain boundary engineering in the SCC behavior of ferritic-martensitic alloy HT-9[J]. Journal of Nuclear Materials,2007(361):160-173.
 
【5】CHO H S,KIMURA A,UKAI S,et al. Corrosion properties of oxide dispersion strengthened steels in superCritical water environment[J]. Journal of Nuclear Materials,2004:329-333.
 
【6】李红梅,蔡珣,吕战鹏,等. 304不锈钢在含硼和锂的高温水中的应力腐蚀破裂和表层氧化膜分析[J]. 材料工程,2004(4):7-10.
 
【7】WAS G S,AMPORNRAT P,GUPTA G,et al. Corrosion and stress corrosion cracking in supercritical water[J]. Journal of Nuclear Materials,2007(371):176-201.
 
相关信息
   标题 相关频次
 超级奥氏体不锈钢HR3C在SCW中的腐蚀行为
 11
 316Ti在超临界水环境中的应力腐蚀和均匀腐蚀行为
 9
 奥氏体不锈钢在含锌PWR一回路水中的均匀腐蚀行为
 8
 25Cr-20Ni-ODS钢在超临界水中的腐蚀行为
 7
 超级奥氏体不锈钢AL-6XN在超临界水环境中的应力腐蚀性能
 7
 P92钢在超临界水中的腐蚀行为
 6
 T91钢在超临界水环境中的腐蚀性能
 6
 高温水中溶解氧对不锈钢堆焊层SCC性能的影响
 6
 压水堆一回路加锌对800合金氧化膜成分影响的XPS分析
 6
 压水堆一回路水中锌含量对镍基690合金氧化膜的影响
 6
 奥氏体不锈钢和镍基合金在550 ℃/25 MPa超临界水中的应力腐蚀开裂敏感性
 5
 超临界水冷堆候选材料的应力腐蚀行为
 4
 合金晶间腐蚀化学浸泡试验方法的适用性
 4
 形变及热处理对国产690合金晶间腐蚀性能影响
 4
 乙醇胺对碳钢腐蚀性能的影响
 4
 用直流电压降法研究316LN不锈钢的疲劳裂纹扩展行为
 4
 304NG奥氏体不锈钢在超临界水环境中的腐蚀行为
 3
 奥氏体不锈钢AL-6XN在超临界水中的腐蚀
 3
 奥氏体不锈钢AL-6XN在超临界水中的腐蚀行为
 3
 海洋环境中受腐蚀混凝土的力学研究现状和展望
 3
 核电厂蒸汽发生器管材800与690合金应力腐蚀性能
 3
 喷丸对800合金在高温碱性溶液中应力腐蚀开裂敏感性的影响
 3
 铅对划伤690合金应力腐蚀行为的影响
 3
 压水堆核电站加锌水化学技术的研究进展
 3
 蒸汽发生器传热管材料划伤诱发应力腐蚀开裂与划伤控制
 3
 Φ219mm×10.5mm弯管环焊缝穿孔失效分析
 2
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 2
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 2
 13Cr不锈钢与Ni基合金油管表面擦划伤的腐蚀行为
 2
 16MnR钢在多种回填材料中的腐蚀行为
 2