6061-T6铝合金搅拌摩擦焊接头的组织和性能
          
Microstructures and Properties of Friction Stir Welded Joint of 6061-T6 Aluminum Alloy

摘    要
对4 mm厚6061-T6铝合金进行了搅拌摩擦焊焊接, 采用组织观察, 拉伸试验和静态腐蚀失重试验对搅拌摩擦焊接头的显微组织和力学性能及腐蚀性能进行了研究。结果表明: 接头焊核区发生了动态再结晶, 形成了细小的等轴晶, 热机影响区晶粒发生了较大程度的变形, 热影响区晶粒发生了粗化; 焊接速度为160 mm·min-1时, 接头的抗拉强度达到215 MPa, 为母材的76%, 接头的断裂形式为韧性断裂; 接头显微硬度分布曲线呈W形, 沿焊缝中心线基本对称, 前进边热影响区硬度低于母材的, 是接头的薄弱环节; 焊接速度为160 mm·min-1时, 焊缝的耐蚀性比母材的好。
标    签 搅拌摩擦焊   6061-T6铝合金   显微组织   力学性能   腐蚀性能   friction stir welding   6061-T6 aluminum alloy   microstructure   mechanical property   corrosion property  
 
Abstract
Aluminum alloy 6061-T6 in thickness of 4 mm was welded by friction stir welding (FSW). The microstructure, mechanical property and corrosion property of FSW joint were investigated by optical microscopy, tensile test and static weight loss experiment. The results demonstrate that the weld nugget zone (WNZ) was characterized by the dynamic recrystallization, which consisted of refined equiaxed grains. The grains in thermo-mechanically affected zone (TMAZ) highly deformed and those in heat-affected zone (HAZ) coarsened. When the welding rate was 160 mm·min-1, the peak tensile strength of the joint reached 215 MPa as much as 76% of the base metal, and the joint fractured as a mode of ductile fracture. Micro-hardness of the joint distributed as W shape and was symmetrically along the welding line. The micro-hardness of the HAZ on advancing side was lower than that of the base metal, where should be the weak zone of the welded joint. The corrosion property of the weld was better than that of the base metal at a welding rate of 160 mm·min-1.

中图分类号 TG453

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 河南省教育厅科学技术研究重点项目(14A460022); 安阳市重大科技计划项目(2013A015); 安阳工学院青年科研基金资助项目(AGQK2013001)

收稿日期 2013/7/30

修改稿日期 2014/6/4

网络出版日期

作者单位点击查看

备注赵亚东(1983-), 男, 河南安阳人, 讲师, 硕士。

引用该论文: ZHAO Ya-dong,ZHANG Yun-zhen,HE Qiang. Microstructures and Properties of Friction Stir Welded Joint of 6061-T6 Aluminum Alloy[J]. Materials for mechancial engineering, 2014, 38(8): 93~96
赵亚东,张运真,何强. 6061-T6铝合金搅拌摩擦焊接头的组织和性能[J]. 机械工程材料, 2014, 38(8): 93~96


被引情况:


【1】宁朝阳,任成高, "6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能",机械工程材料 39, 61-64(2015)

【2】董海荣,马 颖,李伟荣, "AZ31B镁合金搅拌摩擦焊接头的显微组织",机械工程材料 40, 70-74(2016)



论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】DAWES C J. Introduction to friction stir welding and its development[J].Welding and Metal Fabrication,1995,63(1): 13-15.
 
【2】MISHRA R S, MA Z Y. Friction stir welding and processing[J].Materials Science and Engineering,2005,50(12): 1-78.
 
【3】THOMEAS W M, NICHOLAS E D. Friction stir welding for the transportation industries[J].Materials and Design,1997,18(16): 269-273.
 
【4】张腾,何宇庭,伍黎明,等.2524-T3铝合金搅拌摩擦焊对接接头的疲劳性能[J].机械工程材料,2012,36(5): 47-49.
 
【5】李铁龙,杨新岐,王振山,等.焊速对AZ80镁合金搅拌摩擦焊接头成形及组织的影响[J].机械工程材料,2013,37(5): 26-29.
 
【6】SUNGGON L, SANGSHIK K, SUNGIEON K, et al. Tensile behavior of friction stir welded Al 6061-T651[J].Metallurgical and Materials Transactions, 2004, 35(9): 2829-2835.
 
【7】LEE W B, JANG H S. Effect of PWHT on behaviors of precipitates and hardness distribution of 6061 A1 alloy joints by friction stir welding method[J].Materials Science Forum,2004,449: 601-604.
 
【8】于勇征,罗宇,栾国红.影响搅拌摩擦焊金属塑性流动的因素[J].焊接学报,2004,25(5): 117-120.
 
【9】于勇征,罗宇,栾国红,等.铝合金LD10-LF6搅拌摩擦焊的金属塑性流动[J].焊接学报,2004,25(6): 115-118.
 
【10】俞汉青,陈金德.金属塑性成型原理[M].北京: 机械工业出版社,2002.
 
【11】汪建华,姚舜,魏良武,等.搅拌摩擦焊接的传热和力学计算模型[J].焊接学报,2000,21(4): 61-64.
 
【12】PARK S H C, SATO Y S, KOKAWA H. Effect of micro-texture on fracture location in friction stir weld of AZ61 during tensile test[J].Script Materialia,2003,49(2): 161-166.
 
【13】钟群鹏,赵子华.断口学[M].北京: 高等教育出版社,2006.
 
【14】CORRAL J, TRILLO E A, YING L, et al. Corrosion of friction-stir welded aluminum alloys 2024 and 2195[J].Journal of Materials Science Letters,2000,19: 2117-2122.
 
相关信息
   标题 相关频次
 6082-T6铝合金搅拌摩擦焊接头的显微组织与力学性能
 6
 7A60-T6超高强铝合金搅拌摩擦焊接头的组织及性能
 6
 焊接速度对镁/铝异种合金搅拌摩擦焊接头显微组织与力学性能的影响
 6
 5083铝合金搅拌摩擦焊接头的显微组织与力学性能
 5
 6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能
 5
 06Cr19Ni10不锈钢/A283低碳钢扩散焊接接头的显微组织和力学性能
 4
 06Cr20Ni11钢埋弧焊焊缝的显微组织和性能
 4
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 4
 12Cr13钢预热处理工艺参数优化
 4
 12Cr1MoV钢过热器爆管的显微组织和力学性能
 4
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 4
 2024铝合金电子束焊接接头的显微组织与力学性能
 4
 240 MPa级高强IF钢的冷轧压下率和退火温度
 4
 300 MW机组锁口叶片断裂原因分析
 4
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 4
 3D打印18Ni300模具钢的显微组织及力学性能
 4
 5 mm厚6005A-T6铝合金双轴肩搅拌摩擦焊接头的组织及性能
 4
 5 mm厚6082-T6铝合金双轴肩搅拌摩擦焊接头的组织与性能
 4
 600 MPa级热轧双相钢的动态连续冷却转变行为及其热轧卷取工艺的优化
 4
 600 MW机组次末级叶片断裂原因分析
 4
 6061铝合金激光填丝焊接接头的组织与力学性能
 4
 7050铝合金搅拌摩擦焊焊接接头的组织与冲击韧性
 4
 7075/6009铝合金层状复合板材的固溶时效热处理工艺
 4
 960MPa级含钼低碳钢钼含量与热处理工艺的确定
 4
 9Ni钢手工电弧焊和自动埋弧焊接头的组织及力学性能
 4
 AlNiFeCuCoCrVx高熵合金的显微组织与力学性能
 4
 AZ31B镁合金搅拌摩擦焊接头的显微组织
 4
 B-HARD400钢板自动火焰切割热影响区深度的判定
 4
 Domex700MC低合金高强钢药芯焊丝CO2气体保护焊焊接接头的组织与性能
 4
 Fe-17Mn-8Cr合金在多向锻造过程中显微组织与性能的变化
 4