纳米二氧化钛增强聚丙烯复合泡沫材料的性能
          
Properties of Nano-TiO2 Reinforced Polypropylene Foam Composite

摘    要
采用超临界流体技术制备了纳米TiO2增强聚丙烯复合泡沫材料, 用扫描电镜和拉伸试验机等分析了纳米TiO2含量对复合泡沫材料的发泡效果、流动性以及力学性能的影响。结果表明: 纳米TiO2能够显著改善复合泡沫材料的发泡效果, 当纳米TiO2的质量分数为3%时, 发泡效果最佳; 温度为250 ℃时, 随着纳米TiO2含量的增加, 复合泡沫材料的黏度逐渐减小; 纳米TiO2显著地提高了复合泡沫材料的拉伸强度和冲击强度, 纳米TiO2质量分数为3%时, 复合泡沫材料的拉伸强度、冲击强度以及断裂伸长率最好, 分别为35 MPa, 19 kJ ·m-2, 289%。
标    签 聚丙烯   纳米二氧化钛   复合泡沫材料   力学性能   polypropylene   nano-TiO2   foam composite   mechanical property  
 
Abstract
Nano-TiO2 reinforced polypropylene (PP) foam composite was prepared using supercritical fluid technique, and the influences of nano-TiO2 content on the foaming effect, flowability and mechanical properties of the foam composite were investigated by scanning electron microscopy (SEM) and standard tensile testing. Results show that nano-TiO2 could improve the foaming effect of the foam composite. When the content of TiO2 was 3wt%, the foaming effect was the best for the foam composite. The apparent viscosity decreased with the increase of nano-TiO2 content at 250 ℃. Nano-TiO2 could significantly improve the tensile and impact strength of the foam composite. When the mass fraction of TiO2 was 3%, the foam composite had the best tensile strength, impact strength and breaking elongation, which were 35 MPa, 19 kJ·m-2 and 289%, respectively.

中图分类号 TG146.1

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 国家自然科学基金资助项目(51167017)

收稿日期 2013/4/12

修改稿日期 2014/4/6

网络出版日期

作者单位点击查看

备注曾亮(1971-), 男, 甘肃兰州人, 讲师, 学士。

引用该论文: ZENG Liang,SUN Chu-feng,WANG Yan-bin,WANG Ai-jun. Properties of Nano-TiO2 Reinforced Polypropylene Foam Composite[J]. Materials for mechancial engineering, 2014, 38(7): 76~79
曾亮,孙初锋,王彦斌,王爱军. 纳米二氧化钛增强聚丙烯复合泡沫材料的性能[J]. 机械工程材料, 2014, 38(7): 76~79


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】熊丽君,吴璧耀.发泡聚丙烯材料的研究生产现状[J].化工新型材料, 2004, 32(2): 8-11.
 
【2】陈佰全,戴文利,汤红霞.聚丙烯发泡材料的研究进展[J].塑料制造, 2006(12): 55-58.
 
【3】李彩凤,应三九,肖正刚.聚丙烯/纳米二氧化钛复合材料的超临界流体微孔发泡[J].高分子材料科学与工程,2012,28(7):124-131.
 
【4】BURT J G. Storage stabile polyo-lchlorofluoroalkane composition[J].Journal of Cellular Plastics,1978,14(6):341-345.
 
【5】卢子兴, 邹波, 李忠明, 等. 空心微珠填充聚氨酯泡沫塑料的力学性能[J].复合材料学报, 2008, 25(6): 175-180.
 
【6】姜鑫, 杨振国. 玻璃微珠表面改性方法及其对硬质聚氨酯泡沫性能的影响[J].复旦学报: 自然科学版, 2007, 46(3): 297-301.
 
【7】CHALIVENDAR V B, SHUKLA A, BOSE A, et al. Processing and mechanical characterization of lightweight polyurethane composites[J]. Journal of Materials Science,2003,38(8):1631-1643.
 
【8】OKAMOTO M, NAM P H, MAITI P, et al. Biaxial flow-induced alignment of silicate layers in polypropylene/clay nanocomposite foam[J].Nano Letters,2001,9(1):503-505.
 
【9】NAM P H, MAITI P, OKAMOTO M, et al. Foam processing and cellular structure of polypropylene/clay nanocomposites[J]. Polymer Engineering & Science,2002,42(9):1907-1918.
 
【10】MARK A T, JAMES P O. Processing of polypropylene-clay nanocomposites: single-screw extrusion with in-line supercritical carbon dioxide feed versus twin-screw extrusion[J].Journal of Applied Polymer Science,2007,103(2):884-892.
 
【11】HUANG H X, WANG J K. Improving polypropylene microcellular foaming through blending and the addition of nano-calcium carbonate[J].Journal of Applied Polymer Science,2007,106(1):505-513.
 
【12】JIANG X L, BAO J B, LIU T, et al. Microcellular foaming of polypropylene/clay nanocomposites with supercritical carbon dioxide[J]. Journal of Cellular Plastics,2009,45(6):515-538.
 
【13】MARCELO A, IGNACIO V J, VERA R, et al. Study of the cellular structure heterogeneity and anisotropy of polypropylene and polypropylene nanocomposite foams[J]. Polymer Engineering & Science,2009,49(12):2400-2413.
 
【14】ZHU B, ZHA W, YANG J, et al. Layered-silicate based polystyrene nanocomposite microcellular foam using supercritical carbon dioxide as blowing agent[J].Polymer,2010,51(10):2177-2184.
 
【15】曹太山, 何力, 张纯, 等. 纳米蒙脱土对聚丙烯微孔发泡行为的影响[J].塑料, 2009, 38(6): 28-30.
 
【16】COLTON J S, SUH N P. T he Nucleation of microcellular thermoplastic foam with additives (Part I): heoretical considerations[J].Polym Eng Sci, 1987,27:485-493.
 
相关信息
   标题 相关频次
 纳米CaCO3添加量对其改性聚丙烯复合材料发泡效果及力学性能的影响
 11
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 4
 表面处理对剑麻纤维增强聚丙烯复合材料力学性能的影响
 4
 麦秸纤维/聚丙烯复合材料的制备与力学性能
 4
 中空玻璃微珠改性PP泡沫复合材料的发泡效果和力学性能
 4
 1.25Cr0.5MoSi钢的焊接工艺评定
 2
 1060工业纯铝累积叠轧后的力学性能
 2
 1060铝在累积轧制中组织和性能的演变
 2
 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能
 2
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 2
 2 000 t水压机立柱断裂分析
 2
 2024铝合金电子束焊接接头的显微组织与力学性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Mn2SiVBS热轧无缝钢管控冷时的组织与性能
 2
 240 MPa级高强IF钢的冷轧压下率和退火温度
 2
 25Cr2MoVA钢调质规范对力学性能的影响
 2
 2GPa高压处理对铜铝合金显微组织和性能的影响
 2
 300 MW机组锁口叶片断裂原因分析
 2
 3003铝合金无缝管制备过程中的显微组织与力学性能变化
 2
 3D打印18Ni300模具钢的显微组织及力学性能
 2
 40CrNi2Mo钢的低温力学性能
 2
 5083铝合金搅拌摩擦焊接头的显微组织与力学性能
 2
 600 MW机组次末级叶片断裂原因分析
 2
 6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能
 2
 6061-T6铝合金搅拌摩擦焊接头的组织和性能
 2
 6082-T6铝合金搅拌摩擦焊接头的显微组织与力学性能
 2
 60Si2Mn弹簧钢力学性能不合格原因分析
 2
 630 ℃长时时效对G112钢组织和力学性能的影响
 2
 7050铝合金均匀化工艺的确定
 2