低碳板条马氏体钢中大角度界面对解理裂纹扩展的影响机理
          
Influence Mechanism of High Angle Boundary on Propagation of Cleavage Cracks in Low Carbon Lath Martensite Steel

摘    要
利用背散射电子衍射技术研究了0.02C-5Mn低碳板条马氏体钢中大角度界面对冲击断口中解理裂纹扩展或断口附近二次解理裂纹扩展的影响, 以分析该钢韧性的组织控制单元; 依据马氏体变体中理想解理晶面{100}的取向差, 比较了板条束界和板条块界改变解理裂纹扩展方向的能力。结果表明: 解理裂纹或二次解理裂纹扩展时在原奥氏体晶界、板条束界和大部分的板条块界处都发生了大角度转折; 板条块界和板条束界阻碍解理裂纹扩展的能力相近, 板条块是控制板条马氏体钢解理断裂和韧脆转变温度的组织单元。
标    签 低碳马氏体钢   韧性   解理断裂   板条马氏体   low carbon martensitic steel   toughness   cleavage fracture   lath martensite  
 
Abstract
In order to analyze the microstructure unit controlling the toughness of 0.02C-5Mn low-carbon lath martensite steel, the effects of high angle boundaries on the propagation of impact fracture cleavage cracks or the propagation of secondary cleavage cracks near the impact fracture in the steel were studied by electron backscatter diffraction (EBSD). Further more, based on the misorientation of ideal cleavage planes {100} between martensitic variants, the ability of packet and block boundaries to change the propagation direction of cleavage cracks was compared. The results indicate that the cleavage cracks or secondary cleavage cracks were deflected through large angles when crossing through the prior austenite grain boundaries, packet boundaries and most of the block boundaries. The ability of packet and block boundaries to hinder cleavage crack propagation was close. Blocks are the microstructure unit controlling cleavage fracture and ductile to brittle transition temperature of lath martensite.

中图分类号 TG113

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家重点基础研究发展计划项目(2010CB630805); 国家自然科学基金资助项目(51201036)

收稿日期 2014/4/27

修改稿日期 2014/3/24

网络出版日期

作者单位点击查看

备注邓灿明(1988-), 男, 江西抚州人, 硕士。

引用该论文: DENG Can-ming,LI Zhao-dong,SUN Xin-jun,ZHOU Yun,YONG Qi-long. Influence Mechanism of High Angle Boundary on Propagation of Cleavage Cracks in Low Carbon Lath Martensite Steel[J]. Materials for mechancial engineering, 2014, 38(6): 20~24
邓灿明,李昭东,孙新军,周芸,雍岐龙. 低碳板条马氏体钢中大角度界面对解理裂纹扩展的影响机理[J]. 机械工程材料, 2014, 38(6): 20~24


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】MORRIS J W. On the ductile-brittle transition in lath martensitic steel[J].ISIJ Int,2011,51(10):1569-1575.
 
【2】MORRIS J W. Comments on the microstructure and properties of ultrafine grained steel[J].ISIJ Int,2008,48(8):1063-1070.
 
【3】MORRIS J W, GUO Z, KRENN C R, et al. The limits of strength and toughness in steel[J].ISIJ Int,2001,41(6):599-611.
 
【4】LNOUE T, MATSUDA S, OKAMURA Y, et al. The fracture of a low carbon tempered martensite [J].Transactions of JIM,1970,11(1):36-43.
 
【5】李昭东. 变形和合金元素对钢中奥氏体组织形成和分解相变的影响[D].北京: 清华大学, 2011.
 
【6】王春芳. 低合金马氏体钢强韧性组织控制单元的研究[D].北京: 钢铁研究总院, 2008.
 
【7】WANG Chun-fang, WANG Mao-qiu, SHI Jie, et al. Effect of microstructural refinement on the toughness of low carbon martensitic steel[J].Scripta Materialia,2008,58:492-495.
 
【8】WANG C F, WANG M Q, SHI J, et al. Effect of Microstructure refinement on the strength and toughness of low alloy martensitic steel [J].Mater Technol, 2007,23:659-664.
 
【9】董瀚,李桂芬,陈南平.高强度30CrNiMnMoB钢的脆性断裂机理[J].钢铁,1997,32(7):49-53.
 
【10】TOMITA Y, OKABAYASHI K.Effect of microstructure on strength and toughness of heat-treated low alloy structural steels[J].Metallurgical Transactions :A,1986,17 (7):1203-1209.
 
【11】NAYLOR J P. The Influence of the lath morphology on the yield stress and transition temperature of martensitic-bainitic steels [J].Metallurgical Transactions: A, 1979, 10(7): 861-873.
 
【12】MORITO S, TANAKA H, KONISHI R, et al. The morphology and crystallography of lath martensite in Fe-C alloys [J].Acta Materialia, 2003, 51:1789-1799.
 
【13】KITAHARA H, UEJI R, TSUJI N, et al. Crystallographic features of lath martensite in low-carbon steel[J].Acta Materialia, 2006,54: 1279-1288.
 
【14】HUTCHINSON B, HAGSTROM J, KARLSSON O, et al. Microstructures and hardness of as-quenched martensites (0.1-0.5%C)[J].Acta Materialia, 2011,59(14) : 5845-5858.
 
【15】MORITO S, YOSHIDA H, MAKI T,et al. Effect of block size on the strength of lath martensite in low carbon steels[J].Mater Sci Eng: A, 2006,438/440 :438-440.
 
【16】周顺深.钢脆性和工程结构脆性断裂[M].上海: 上海科学技术出版社, 1983.
 
【17】王小勇, 潘涛, 王华, 等.Ni-Cr-Mo-B超厚钢板表面低碳回火马氏体组织的韧性研究[J].金属学报,2012,48(4): 401-406.
 
【18】由洋, 王学敏, 尚成嘉.奥氏体化温度对HSLA100高强度低合金钢组织及冲击韧性的影响[J].金属学报,2012,48(11):1290-1298.
 
【19】张小立, 庄传晶, 吉玲康, 等.高钢级管线钢的有效晶粒尺寸[J].机械工程材料,2007,31(3): 4-8.
 
相关信息
   标题 相关频次
 热处理工艺对Ti55531钛合金显微组织与拉伸性能的影响
 6
 初始损伤对不同钢组织缺口试样解理断裂韧性的影响
 4
 低合金超高强度钢的研究进展
 4
 22Cr双相不锈钢锻件韧性下降原因分析
 2
 35钢螺钉断裂分析
 2
 60Si2Mn弹簧扁钢崩料断裂原因分析
 2
 DZ55钢级φ102 mm×9.19 mm地质钻杆管体断裂原因分析
 2
 L360M管线钢管水压爆破试验开裂分析
 2
 NF709R耐热钢高温长时时效后的组织和性能
 2
 PH13-8Mo高强不锈钢在不同温度时效后的析出相及其对力学性能的影响
 2
 Q&P钢的显微组织及力学性能
 2
 Super304H钢700 ℃时效后组织和韧性的变化
 2
 X70管线钢焊接接头热影响区的冲击性能
 2
 不同调质热处理X80钢厚板的组织与性能
 2
 超低碳烘烤硬化钢板的烘烤硬化性能
 2
 超低碳微合金管线钢焊接接头的组织与冲击性能
 2
 脆性温度点时效对22Cr双相不锈钢冲击性能的影响
 2
 低碳高铌微合金钢的析出行为
 2
 锻造工艺对铌-钒微合金非调质钢显微组织的影响
 2
 风机联轴器断裂原因分析
 2
 高强度特厚Q460钢板的轧制工艺与力学性能
 2
 机械镀锌层在冲击条件下的失效行为
 2
 挤压-烧结法制备铁铬铝金属蜂窝的组织与性能
 2
 夹杂物和晶粒尺寸对洁净车轮钢室温冲击韧度的影响
 2
 马蹄形卸扣断裂原因分析
 2
 条形微裂纹对16MnR钢解理断裂韧性的影响
 2
 铜含量对高铬铁素体钢组织和蠕变性能的影响
 2
 一种新型高铬铁素体钢的蠕变性能及显微组织
 2
 影响球墨铸铁曲轴质量的因素
 2
 中碳铬-镍-钼钢的超高强度和超低屈强比现象
 2