纳米CaCO3添加量对其改性聚丙烯复合材料发泡效果及力学性能的影响
          
Effects of Nano-CaCO3 Addition on Foamed Effect and Mechanical Properties of Polypropylene Composite Modified by Nano-CaCO3

摘    要
采用超临界流体技术制备出纳米CaCO3改性聚丙烯复合材料, 研究了纳米CaCO3添加量对复合材料发泡效果、力学性能以及CaCO3和聚丙烯共混物流变性能的影响。结果表明: 随纳米CaCO3添加量的增多, 复合材料的发泡效果先变好再变差, 而拉伸强度和冲击韧度均先升后降, 当纳米CaCO3质量分数为5%时, 复合材料的发泡效果最佳, 拉伸强度和冲击韧度最大, 分别为16 MPa和37 kJ·m-2; 在250 ℃时, 随着纳米CaCO3添加量的增大, 共混物的表观黏度逐渐减小。
标    签 聚丙烯   纳米碳酸钙   复合材料   发泡效果   力学性能   polypropylene (PP)   nano-CaCO3   composite   foamed effect   mechanical property  
 
Abstract
Nano-CaCO3 modified polypropylene composites were prepared using supercutical fluid technology, and the effects of nano-CaCO3 on foamed effect and mechanical properties of the composite, and on the rheological property of blend including CaCO3 and polypropylene were studied. The results show that the foamed effect of the composite was first good and then poor, and the tensile strength and impact toughness all increased and then decreased with the increase of nano-CaCO3 addition. When the addition of nano-CaCO3 was 5wt%, the composite had the best foamed effect and mechanical properties, the tensile strength and impact toughness were 16 MPa and 37 kJ·m-2, respectively. The apparent visconsity of the blend decreased gradually with the increase of the nano-CaCO3 addition at 250 ℃.

中图分类号 TQ328.9

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及其应用

基金项目 国家自然科学基金资助项目(51167017)

收稿日期 2012/12/27

修改稿日期 2013/11/14

网络出版日期

作者单位点击查看

备注孙初锋(1977-), 男, 山东威海人, 副教授, 博士。

引用该论文: SUN Chu-feng,WANG Yan-bin,ZENG Liang,WANG Ai-jun. Effects of Nano-CaCO3 Addition on Foamed Effect and Mechanical Properties of Polypropylene Composite Modified by Nano-CaCO3[J]. Materials for mechancial engineering, 2014, 38(2): 68~71
孙初锋,王彦斌,曾亮,王爱军. 纳米CaCO3添加量对其改性聚丙烯复合材料发泡效果及力学性能的影响[J]. 机械工程材料, 2014, 38(2): 68~71


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】熊丽君,吴璧耀.发泡聚丙烯材料的研究生产现状[J].化工新型材料, 2004, 32(2): 8-11.
 
【2】陈佰全,戴文利,汤红霞.聚丙烯发泡材料的研究进展[J].塑料制造, 2006(12): 55-58.
 
【3】卢子兴,邹波,李忠明,等.空心微珠填充聚氨酯泡沫塑料的力学性能[J].复合材料学报, 2008, 25(6): 175-180.
 
【4】姜鑫, 杨振国. 玻璃微珠表面改性方法及其对硬质聚氨酯泡沫性能的影响[J].复旦学报: 自然科学版, 2007, 46(3): 297-301.
 
【5】CHALIVENDAR V B, SHUKLA A, BOSE A, et al. Processing and mechanical characterization of lightweight polyurethane composites[J].Journal of Materials Science,2003,38(8):1631-1643.
 
【6】OKAMOTO M, NAM P H, MAITI P, et al. Biaxial flow-induced alignment of silicate layers in polypropylene/clay nanocomposite foam[J].Nano Letters,2001,9(1):503-505.
 
【7】NAM P H, MAITI P, OKAMOTO M, et al. Foam processing and cellular structure of polypropylene/clay nanocomposites[J].Polymer Engineering&Science,2002,42(9):1907-1918.
 
【8】MARK A T, JAMES P O. Processing of polypropylene-clay nanocomposites: single-screw extrusion with in-line supercritical carbon dioxide feed versus twin-screw extrusion[J].Journal of Applied Polymer Science,2007,103(2):884-892.
 
【9】HUANG H X, WANG J K. Improving polypropylene microcellular foaming through blending and the addition of nano-calcium carbonate[J]. Journal of Applied Polymer Science,2007,106(1):505-513.
 
【10】JIANG X L, BAO J B, LIU T, et al. Microcellular foaming of polypropylene/clay nanocomposites with supercritical carbon dioxide [J]. Journal of Cellular Plastics,2009,45(6):515-538.
 
【11】MARCELO A, IGNACIO V J, VERA R, et al. Study of the cellular structure heterogeneity and anisotropy of polypropylene and polypropylene nanocomposite foams[J].Polymer Engineering&Science,2009,49(12):2400-2413.
 
【12】ZHU B, ZHA W, YANG J, et al. Layered-silicate based polystyrene nanocomposite microcellular foam using supercritical carbon dioxide as blowing agent[J].Polymer,2010,51(10):2177-2184.
 
【13】曹太山,何力,张纯, 等.纳米蒙脱土对聚丙烯微孔发泡行为的影响[J].塑料, 2009, 38(6): 28-30.
 
【14】许忠斌, 吴舜英, 黄步明, 等.微孔塑料注射成型机理及其技术发展动向[J].轻工机械,2003(4):24-28.
 
相关信息
   标题 相关频次
 纳米二氧化钛增强聚丙烯复合泡沫材料的性能
 11
 PP-g-MAH改性SGF+POE/FPP复合材料的制备及性能
 5
 Ca-α/β-Sialon结合刚玉复合材料的力学性能
 4
 MGF/PLA复合材料的制备及性能
 4
 包覆镍CNTs/AM60复合材料铸态显微组织与力学性能
 4
 包覆镍的碳纳米管增强AZ91镁基复合材料的显微组织与力学性能
 4
 芳纶纤维增强尼龙6复合材料的制备与性能
 4
 纳米碳酸钙对填充型粉末丁苯橡胶硫化胶力学性能的影响
 4
 偶联剂表面处理对纳米SiO2/氰酸酯树脂复合材料力学性能的影响
 4
 石墨烯增强AZ91镁基复合材料的力学性能
 4
 碳纳米管/酚醛树脂基复合材料的研究进展
 4
 苎麻增强环氧树脂复合材料的力学性能
 4
 表面处理对剑麻纤维增强聚丙烯复合材料力学性能的影响
 3
 风力机叶片用复合材料的拉伸及冲蚀磨损性能
 3
 麦秸纤维/聚丙烯复合材料的制备与力学性能
 3
 熔渗法制备高强Mg(AZ91D)/NiTi阻尼复合材料及其压缩和阻尼性能
 3
 中空玻璃微珠改性PP泡沫复合材料的发泡效果和力学性能
 3
 1.25Cr0.5MoSi钢的焊接工艺评定
 2
 1060工业纯铝累积叠轧后的力学性能
 2
 1060铝在累积轧制中组织和性能的演变
 2
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 2
 12Cr13钢预热处理工艺参数优化
 2
 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能
 2
 15Ni3CrMoV与10Ni5CrMoV异种钢对接接头的显微组织及力学性能
 2
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 2
 2 000 t水压机立柱断裂分析
 2
 2024铝合金电子束焊接接头的显微组织与力学性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Mn2SiVBS热轧无缝钢管控冷时的组织与性能
 2