新淬火状态2A12铝合金的成形极限
          
Forming Limit for As-quenched 2A12 Aluminum Alloy

摘    要
对室温下分别时效10,20,30 min的9种尺寸新淬火状态2A12铝合金试样在3种润滑(固体润滑,液体润滑和无润滑)条件下进行了胀形试验,得到了该铝合金的成形极限图,分析了时效时间对成形性能的影响。结果表明:时效10 min时新淬火状态2A12铝合金仍具备良好的成形性能,但随时效时间的延长,成形极限曲线下移,铝合金的塑性变差,成形安全区变小;2A12铝合金成形加工前的自然时效时间应控制在10 min以内。
标    签 2A12铝合金   新淬火   自然时效   成形极限   2A12 aluminum alloy   as-quenching   natural aging   forming limit  
 
Abstract
As-quenched 2A12 aluminum alloy specimens with nine kinds of size obtained after aging at room temperature for 10, 20, 30 min, respectively, were bulged under three types of lubrication conditions including solid lubrication, liquid lubrication and no lubrication, respectively. The forming limit diagram of the aluminum alloy was obtained, and the effect of aging time on the formability was analyzed. The results show that the as-quenched 2A12 aluminum alloy obtained after aging for 10 min had good formability. With the increase of aging time, the forming limit curves moved down, indicating that the plasticity of the aluminum alloy decreased and the forming safety area became smaller. The appropriate natural aging time of 2A12 aluminum alloy before forming was within 10 min.

中图分类号 V250.3   DOI 10.11973/jxgccl201806011

 
  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2017/5/12

修改稿日期 2018/5/15

网络出版日期

作者单位点击查看

备注张鹏(1989-),男,吉林长春人,博士研究生

引用该论文: ZHANG Peng,CHEN Minghe,YE Jianhua. Forming Limit for As-quenched 2A12 Aluminum Alloy[J]. Materials for mechancial engineering, 2018, 42(6): 55~58
张鹏,陈明和,叶建华. 新淬火状态2A12铝合金的成形极限[J]. 机械工程材料, 2018, 42(6): 55~58


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】中国航空材料手册编委会.中国航空材料手册:第三卷[M]. 北京:中国标准出版社,2002.
 
【2】飞机设计手册总编委会.飞机设计手册:第3册上[M].北京:航空工业出版社,2004.
 
【3】KEELER S P, BACKOFEN W A. Plastic instability and fracture in sheets stretched over rigid punches[J]. Trans ASM Q, 1963,56(1):25-48.
 
【4】GOODWIN G M. Application of strain analysis to sheet metal forming problems in the press shop[C]//1968 Automotive Engineering Congress and Exposition.[S.l.]:SAE, 1968:680093.
 
【5】王辉. 成形极限图的获取方法与其在金属板料成形中的应用[D].南京:南京航空航天大学,2011.
 
【6】陈明和, 高霖, 薛玉雷,等. 板料应力成形极限判据的有限元分析程序[J].南京航空航天大学学报,2005,37(增刊1):68-71.
 
【7】张成祥, 陈明和, 雷晓晶, 等. GH600合金薄板成形极限研究[J]. 航空材料学报, 2015, 35(6):35-40.
 
【8】张成祥, 陈明和, 雷晓晶,等. GH163合金成形极限图及应用[J]. 塑性工程学报, 2016, 23(1):93-98.
 
【9】高宏志, 周贤宾. 新淬火状态铝合金板的成形极限[J]. 北京航空航天大学学报, 2006, 32(9):1083-1086.
 
【10】高宏志, 周贤宾. 新淬火状态硬铝合金板的成形性能及数值模拟[J]. 航空材料学报, 2008, 28(5):27-31.
 
【11】黄华, 李大永, 彭颖红. 7075-T6铝合金板温热成形极限图实验[J]. 塑性工程学报, 2010, 17(1):93-97.
 
【12】陈劫实, 周贤宾. 板料成形极限预测新判据[J]. 机械工程学报, 2009, 45(4):64-69.
 
【13】DOEGE E, DRÖDER K. Sheet metal forming of magnesium wrought alloys:Formability and process technology[J]. Journal of Materials Processing Technology, 2001, 115(1):14-19.
 
【14】LI D M, GHOSH A. Tensile deformation behavior of aluminum alloys at warm forming temperatures[J]. Materials Science and Engineering:A, 2003, 352(1/2):279-286.
 
相关信息
   标题 相关频次
 2A12铝合金不同方法腐蚀疲劳的寿命及断口形貌
 2
 2A12铝合金弹性常数数字图像相关测试法及其参数灵敏度分析
 2
 7075铝合金的同步冷却热成形工艺
 2
 Al-Mg-Si基合金车身板材成形极限及数值应用
 2
 Cl-浓度对2A12铝合金电化学行为的影响
 2
 HEDP对1Cr18Ni9Ti在硝酸中腐蚀行为的影响
 2
 X80钢在0.5 mol/L NaCl溶液中的交流电流腐蚀行为
 2
 X射线荧光光谱法测定合金中的磷
 2
 X射线荧光光谱法测定耐指纹板有机涂层中二氧化硅
 2
 不同温度下X80钢在高pH土壤模拟溶液中的腐蚀电化学行为
 2
 差厚激光拼焊板的成形极限
 2
 地铁受电弓预调螺杆断裂失效分析
 2
 非完全消化-火焰原子吸收光谱法测定水果中铜铁锌
 2
 焊丝对2A12铝合金焊接接头组织和力学性能的影响
 2
 基于Weibull分布研究激光-电弧复合焊接接头的力学性能
 2
 基于风险检测技术在某海上油气田装置腐蚀风险预测的应用
 2
 基于韧性断裂的汽车用铝合金板滚压包边成形开裂预测
 2
 基于韧性断裂准则用有限元方法预测镍涂层薄钢板的成形极限
 2
 基于最大二阶主应变和Savitzky-Golay平滑原理对热轧酸洗板成形极限的数值模拟
 2
 交流电流作用下X80钢在碱性溶液中阴极保护准则的适用性能
 2
 冷轧薄板成形性能研究的内容和方法
 2
 冷轧低碳钢带人工时效与自然时效行为分析
 2
 钛加铌共处理的高强无间隙原子钢铁素体区高温拉伸流变应力方程及热加工图
 2
 重熔渣系对一种铁基高温合金电渣锭冶金质量的影响
 2
 自然时效及受到辐照时玻璃钢管道声学与力学性能的关联性
 2
 BTi6431S高温钛合金盒形件超塑性成型工艺
 1
 LY12M铝合金板同步冷却热拉伸后的组织与性能
 1
 TC1钛合金的高温流变行为
 1
 Ti2AlNb合金的高温拉伸变形行为
 1
 X80钢在0.5 mol/L NaHCO3溶液中的交流电流腐蚀行为
 1