电压和激光模式对三维原子探针测试结果的影响
          
Effects of Voltage and Laser Modes on Test Results of Three-Dimensional Atom Probe

摘    要
将Fe-CuMnNiAl钢淬火后在450 ℃回火4 h,分别在电压和激光模式下,用三维原子探针(3DAP)对其进行测试,对比研究了两种模式对测试结果的影响。结果表明:与电压模式相比,激光模式下的数据背底较小,质量分辨率较好,成分分析结果较准确,蒸发离子价态二价减少,一价增多,甚至出现两个原子同时蒸发的离子团;另外,激光模式下测得的析出相尺寸稍大,数量密度稍低,析出相核心铜元素含量较低。
标    签 电压模式   激光模式   三维原子探针(3DAP)   析出相   voltage mode   laser mode   three-dimensional atom probe (3DAP)   precipitate  
 
Abstract
Fe-CuMnNiAl steel was quenched to room temperature and then tempered at 450℃ for 4 h. The tempered steel specimens were tested by three-dimensional atom probe (3DAP) under voltage mode and laser mode respectively to study the effects of different modes on the test results. The results show that the background of the data was smaller, the mass resolution was higher, the composition analysis results was more accurate under the laser mode compared with those under the voltage mode. Under the laser mode, the divalent evaporation ions were reduced, while the monovalent ions increased, and two atom group evaporated at the same time even more. It is found that the precipitate was bigger in size and was slightly lower in density under the laser mode than under the voltage mode, and the core Cu content of precipitate was lower under the laser mode.

中图分类号 TH87   DOI 10.11973/lhjy-wl201806001

 
  中国光学期刊网论文下载说明


所属栏目 试验与研究

基金项目 国家重点研发计划资助项目(No.2016YFB0700401);国家自然科学基金委员会-中国工程物理研究院NSAF联合基金资助项目(No.U1530115);上海市科学技术委员会重点项目(12JC1404000);上海市科委科学仪器化学试剂专项(17142203100)

收稿日期 2017/7/11

修改稿日期

网络出版日期

作者单位点击查看


备注沈琴(1992-),女,博士研究生,主要从事金属材料中纳米析出相研究

引用该论文: SHEN Qin,WANG Zemin,LI Hui,LIU Wenqing. Effects of Voltage and Laser Modes on Test Results of Three-Dimensional Atom Probe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(6): 385~389
沈琴,王泽民,李慧,刘文庆. 电压和激光模式对三维原子探针测试结果的影响[J]. 理化检验-物理分册, 2018, 54(6): 385~389


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】LIU Q D,ZHAO S J. Cu precipitation on dislocation and interface in quench-aged steel[J]. MRS Communications,2012,2(4):127-132.
 
【2】LI H,XIA S,ZHOU B X,et al. C-Cr segregation at grain boundary before the carbide nucleation in alloy 690[J]. Materials Characterization,2012,66:68-74.
 
【3】WANG X J,SHA G,SHEN Q,et al. Age-hardening effect and formation of nanoscale composite precipitates in a NiAlMnCu-containing steel[J]. Materials Science and Engineering:A,2015,627:340-347.
 
【4】SHEN Q,CHEN H,LIU W Q. Effect of Cu on nanoscale precipitation evolution and mechanical properties of a Fe-NiAl alloy[J]. Microscopy and Microanalysis,2017,23(2):350-359.
 
【5】WANG Z M,FANG X L,LI H,et al. Atom probe tomographic characterization of nanoscale Cu-rich precipitates in 17-4 precipitate hardened stainless steel tempered at different temperatures[J]. Microscopy and Microanalysis,2017,23(2):340-349.
 
【6】徐刚,蔡琳玲,冯柳,等. 利用APT对RPV模拟钢中界面上原子偏聚特征的研究[J]. 金属学报,2012,48(7):789-796.
 
【7】MILLER M K,FORBES R G. Atom probe tomography[J]. Materials Characterization,2009,60(6):461-469.
 
【8】VELLA A,VURPILLOT F,GAULT B,et al. Evidence of field evaporation assisted by nonlinear optical rectification induced by ultrafast laser[J]. Physical Review: B,2006,73: 165416.
 
【9】CEREZO A,CLIFTON P H,GOMBERG A,et al. Aspects of the performance of a femtosecond laser-pulsed 3-dimensional atom probe[J]. Ultramicroscopy,2007,107(9):720-725.
 
【10】BLAVETTE D,KASSAB A T,CADEL E,et al. Laser-assisted atom probe tomography and nanosciences[J]. International Journal of Materials Research,2008,99(5):454-460.
 
【11】巴发海,李勇,李凯. 新版X射线残余应力测定国标中的新技术与新要求[J]. 理化检验(物理分册),2017,53(9):615-623.
 
相关信息
   标题 相关频次
 分析室真空度对原子探针测试数据质量的影响
 3
 铌-钒微合金钢中碳氮化合物的析出特点
 3
 630 ℃长时时效对G112钢组织和力学性能的影响
 2
 N18锆合金的疖状腐蚀
 2
 不同工艺热处理后超高强Cu-15Ni-8Sn-Zn-0.8Al-0.2Si合金的腐蚀行为
 2
 常减压装置环烷酸腐蚀的缓蚀剂研究
 2
 吹扫捕集-气相色谱-质谱联用法测定水中挥发性卤代烃和氯苯
 2
 复合能场铸轧和普通铸轧AZ31B镁合金板轧制后的组织与力学性能
 2
 高温拉伸试验进行NADCAP认证时应注意的技术要点
 2
 固溶和时效对0Cr21Ni6Mn9N含氮奥氏体不锈钢组织的影响
 2
 几种常用的脱碳层深度测定方法
 2
 铰链梁铰耳断裂原因分析
 2
 金属材料高温拉伸试验过程要点分析
 2
 扩散退火对Inconel 783合金显微组织及力学性能的影响
 2
 氢化物发生-原子荧光光谱法测定茶叶总硒时样品前处理方法的比较
 2
 热处理工艺对高锰奥氏体热作模具钢组织和性能的影响
 2
 塑料激光焊接技术的研究进展
 2
 钛对LF9镍基合金力学性能的影响
 2
 体心立方近β钛合金循环形变中的平面滑移行为
 2
 一种新型高铬铁素体钢的蠕变性能及显微组织
 2
 应力控制下7075-T651铝合金的疲劳断裂行为
 2
 油气钻井工程中的腐蚀防护及一种强激光与粒子束新的防护方法
 2
 1900MPa级超高强度不锈钢的研制
 1
 20MnSiNb钢的显微组织及其对屈服行为的影响
 1
 650 ℃时效不同时间后Super304H钢的显微组织
 1
 700 ℃长时时效对LF2合金组织和高温拉伸性能的影响
 1
 7150铝合金在热压缩变形过程中的动态组织演变
 1
 H13钢外套早期开裂分析
 1
 NF709R耐热钢高温长时时效后的组织和性能
 1
 PH13-8Mo高强不锈钢在不同温度时效后的析出相及其对力学性能的影响
 1