地下不锈钢供水管道腐蚀渗漏失效分析
          
Corrosion Failure Analysis of an Underground Stainless Steel Pipeline for Water Supply

摘    要
利用扫描电子显微镜、能量色散X射线谱等技术手段,对某公司建设的地下不锈钢供水管道腐蚀渗漏现象进行了失效分析。分析结果显示:失效不锈钢管的化学成分、力学性能和金相组织均符合国家标准对S30408(06Cr19Ni10)不锈钢的要求;不锈钢管的腐蚀破坏由内壁开始,部分区域穿透整个壁厚形成渗漏点;失效不锈钢管的渗漏是由氯离子点腐蚀及晶间腐蚀引起的。
标    签 304不锈钢管道   氯离子   点腐蚀   晶间腐蚀   304 stainless steel pipe   chloride ion   pitting   intergranular corrosion  
 
Abstract
The failure analysis of corrosion leakage of an underground stainless steel pipeline for water supply constructed by a company was performed using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The analysis results show that the chemical composition, mechanical properties and microstructure of the failure pipe were consistent with the standard requirements for S30408(06Cr19Ni10) stainless steel. The corrosion damage occurred on the inner surface of the stainless steel pipe initially. Pitting and intergranular corrosion caused by chloride ion were the main cause of the failure of the stainless steel pipe.

中图分类号 TG172   DOI 10.11973/fsyfh-201806015

 
  中国光学期刊网论文下载说明


所属栏目 失效分析

基金项目 国家自然科学基金(11404192);山东省“泰山学者海外特聘专家”专项经费(tshw20120745);山东省优秀中青年科学家科研奖励基金(BS2014CL002);山东省重点研发计划项目(2017GSF220004);山东省科学院科研项目[2017QN001;科基合字(2018)第5号]

收稿日期 2017/2/7

修改稿日期

网络出版日期

作者单位点击查看


引用该论文: CHEN Lizong,SHI Junbo,XU Na,LIU Long,DING Ning,GUO Weimin,HU Zhiwen. Corrosion Failure Analysis of an Underground Stainless Steel Pipeline for Water Supply[J]. Corrosion & Protection, 2018, 39(6): 484


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】周凯文. 新型绿色环保给水管材-薄壁不锈钢管[J]. 建筑施工,2008,30:711-712.
 
【2】王海涛. 浅谈薄壁不锈钢管在给排水管材中的应用[J]. 国外建材科技,2006,27:85-86.
 
【3】时军波,陈立宗,丁宁,等. 热交换器不锈钢传热板片的腐蚀失效原因[J]. 腐蚀与防护,2016,37(1):71-75.
 
【4】MARTINS C M B,MOREIRA J L,MARTINS J I. Corrosion in water supply pipe stainless steel 304 and a supply line of helium in stainless steel 316[J]. Eng Fail Anal,2014,39:65-71.
 
【5】YANG G,YOON K B,MOON Y C. Stress corrosion cracking of stainless steel pips for methyl-methacrylate process plants[J]. Eng Fail Anal,2013,29:45-55.
 
【6】SMIDERLE J,PARDAL J M,TAVARES S S M,et al. Premature failure of superduplex stainless steel pipe by pitting in sea water environment[J]. Eng Fail Anal,2014,46:134-139.
 
【7】鞠虹,王君,唐晓,等. 油气集输管道在海洋环境中的腐蚀与防护[J]. 石油化工设备,2010,39:41-47.
 
【8】NATALIE C A. Thermodynamics of aqueous corrosion in ASM Handbook[M].[S.l.]:ASM International,2002:18-86.
 
【9】金志浩,葛红花,林薇薇,等. 四种不锈钢在含不同浓度Cl-的高炉煤气管道冷凝模拟液中的腐蚀行为[J]. 腐蚀与防护,2014,35(9):890-894.
 
相关信息
   标题 相关频次
 电气火灾中铜导线熔痕的微观特征
 12
 汽车冷却装置护板断裂的原因
 12
 热交换器不锈钢传热板片的腐蚀失效原因
 9
 Q235B彩钢板的腐蚀原因分析
 4
 电气火灾中导线熔痕的宏微观特征
 4
 金相分析技术在电气火灾原因鉴定中的应用
 4
 热轧碳素钢板断后伸长率与试样尺寸的关系
 4
 1Cr18Ni9Ti奥氏体不锈钢薄板断后伸长率的换算
 3
 Cr12钢冷冲模具加工过程中开裂原因分析
 3
 不锈钢丝网断裂原因分析
 3
 0Cr18Ni9不锈钢换热管应力腐蚀开裂原因分析
 2
 18-8奥氏体不锈钢焊接接头晶间腐蚀的评定及控制
 2
 2197铝锂合金在不同热处理状态下的晶间腐蚀及剥蚀行为
 2
 304不锈钢表面直流磁控溅射钛膜的耐蚀性
 2
 304不锈钢薄壁容器焊缝腐蚀泄漏原因
 2
 304和316L管材在两类模拟介质中的晶间腐蚀形貌
 2
 316L-16MnR复合板不锈钢侧晶间腐蚀原因分析
 2
 316L不锈钢在普光净化厂含氯胺液中的应力腐蚀开裂
 2
 7075-TiB2原位铝基复合材料的腐蚀性能
 2
 800H合金旋风分离器壳体失效分析
 2
 9Cr18合金的燃气热腐蚀行为
 2
 C22哈氏合金换热器腐蚀原因及其防护措施
 2
 Cl-浓度对2A12铝合金电化学行为的影响
 2
 Cr12MoV钢模具线切割开裂原因分析
 2
 D210塔筒体泄漏原因分析
 2
 EPR法在评价304L不锈钢晶间腐蚀敏感性中的应用
 2
 HSn70-1船用冷凝管腐蚀穿孔失效分析
 2
 Incoloy825合金TIG和PAW焊接接头耐晶间腐蚀性能的对比
 2
 Inconel 800合金波纹管开裂的原因
 2
 PTA装置碱洗对设备腐蚀开裂影响讨论
 2