T91钢在5.0% NaCl中性盐雾中的腐蚀行为
          
Corrosion Behavior of T91 Steel in Neutral Salt Spray with 5.0% NaCl Solution

摘    要
通过腐蚀质量损失分析,宏、微观腐蚀形貌观察及腐蚀产物分析等方法研究了T91钢在5.0%(质量分数)NaCl中性盐雾中的腐蚀行为。结果表明:在盐雾腐蚀过程的前75 h,T91钢的腐蚀速率较低,表面腐蚀产物生长缓慢,75 h后T91钢的腐蚀速率急剧增大,表面腐蚀产物快速增多增厚;T91钢表面的腐蚀产物主要为Fe和Cr的氧化物;T91钢表面首先产生局部腐蚀,进而发展成腐蚀斑,最后腐蚀斑底部产生新的局部腐蚀。
标    签 T91钢   中性盐雾试验   局部腐蚀   T91 steel   neutral salt spray test   localized corrosion  
 
Abstract
The corrosion behavior of T91 steel in neutral salt spray with 5% (mass) NaCl solution was studied by mass loss analysis, macro and micro morphology observation and corrosion product analysis. The results show that in the first 75 h of salt spray corrosion, the corrosion rate of T91 steel was low, and the surface corrosion products grew slowly; after 75 h, the corrosion rate of T91 steel sharply increased, and the surface corrosion products rapidly increased in quantity and thickness. The corrosion products on the T91 steel surface were mainly composed of oxides of Fe and Cr. The T91 steel surface first generated localized corrosion, and then the localized corrosion developed into corrosion pits. Finally, new localized corrosion occurred at the bottom of the corrosion pits.

中图分类号 TG172.4   DOI 10.11973/fsyfh-201806004

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 国家自然科学基金项目(51601164);中国博士后科学基金(2017M622594)

收稿日期 2017/1/20

修改稿日期

网络出版日期

作者单位点击查看


引用该论文: FENG Chao,PENG Bicao,XIE Yi,WANG Jun,LI Minghuan,LIU Yongxiong,WU Tangqing,YIN Fucheng. Corrosion Behavior of T91 Steel in Neutral Salt Spray with 5.0% NaCl Solution[J]. Corrosion & Protection, 2018, 39(6): 431


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】OTOGURO Y,MATSUBARA M,ITOH I,et al. Creep rupture strength of heat affected zone for 9Cr ferritic heat resisting steels[J]. Nuclear Engineering and Design,2000,196(1):51-61.
 
【2】REN X,SRIDHARAN K,ALLEN T R. Corrosion of ferritic-martensitic steel HT9 in supercritical water[J]. Journal of Nuclear Materials,2006,358(2/3):227-234.
 
【3】CHEN Y,SRIDHARAN K,ALLEN T. Corrosion behavior of ferritic-martensitic steel T91 in supercritical water[J]. Corrosion Science,2006,48(9):2843-2854.
 
【4】KOFSTAD P. High temperature corrosion[M]. London:Elsevier Applied Science Publishers Ltd.,1988.
 
【5】张都清,徐敬军,赵国群,等. 9Cr-1Mo钢在含水蒸汽气氛中的氧化行为[J]. 材料研究学报,2008,22(6):599-605.
 
【6】高文华,沈朝,张乐福. T91钢在超临界水环境中的腐蚀性能[J]. 腐蚀与防护,2016,37(6):444-502.
 
【7】张清廉,王起江,刘彩玲. 抛光态T91无缝管腐蚀原因分析[J]. 宝钢技术,2014(4):61-65.
 
【8】余菲,袁曹龙,蒋娅,等. pH值、离子浓度、温度对T23与T92电化学腐蚀行为的影响[J]. 全面腐蚀控制,2010,24(4):6-10.
 
相关信息
   标题 相关频次
 新V型内聚光CPC热管式真空管集热器的热性能
 3
 5083铝壳艇外加电流阴极保护系统研制
 2
 CR技术与胶片照相技术的特性对比试验
 2
 GIS设备导体缺陷X射线数字成像检测及缺陷产生原因分析
 2
 P110油管腐蚀穿孔分析
 2
 T91/P91钢管焊接接头的超声波探伤
 2
 T91钢管手工氩弧焊接头的显微组织
 2
 T91钢和TP304钢对含氯盐水蒸气的抗氧化性能
 2
 T91钢在650 ℃时效过程中析出相的变化
 2
 TP347H耐热钢管在超临界条件下的氧化膜结构及形成机理
 2
 X65管线钢在模拟海水环境中的腐蚀行为
 2
 X70钢焊接接头在酸性溶液中的局部腐蚀SVET研究
 2
 X70管线钢CO2湿气顶部的腐蚀行为
 2
 包覆层管道内壁局部腐蚀脉冲涡流检测探头的性能比较
 2
 保温原油储罐外壁腐蚀成因及防腐蚀措施
 2
 苯丙胺与牛血清白蛋白相互作用机理的研究
 2
 不锈钢腐蚀评价技术研究及其应用
 2
 采用加压瞬间液相连接技术焊接T91钢管
 2
 长时运行后高温再热器T91钢管的冲击韧性
 2
 常压储罐底板腐蚀速率与声发射活度的相关性探讨
 2
 超超临界机组锅炉异种钢小径管镍基焊接接头超声波检测
 2
 超超临界机组锅炉用T91钢蒸汽采样管焊接接头开裂的原因
 2
 超-超临界汽轮机转子材料T91钢的堆焊修复
 2
 沉积砂对X60钢在饱和CO2油田水中腐蚀行为的影响
 2
 成品油储罐T形焊缝腐蚀控制
 2
 稠油热采管BG90H钢在不同条件下的腐蚀行为
 2
 从ISO17636-2标准看数字射线检测技术的发展趋势
 2
 放电等离子烧结42CrMo钢/黄铜双金属复合接头的显微组织
 2
 钙和锶对Mg2Si/AZ91D复合材料组织和性能的影响
 2
 钢网架用高强螺栓的断裂原因分析
 2