海洋工程紧固件用0Cr20Mn18N0.8高氮奥氏体不锈钢的性能
          
Property of 0Cr20Mn18N0.8 High Nitrogen Austenite Stainless Steel for Marine Engineering Fasteners

摘    要
新开发了一种0Cr20Mn18N0.8高氮奥氏体不锈钢,研究了其静拉伸、缺口拉伸、偏斜拉伸、冲击、疲劳以及耐腐蚀等性能,并与316L不锈钢的进行了对比,分析了该钢用于海洋工程紧固件的可行性。结果表明:试验钢的静拉伸屈服强度和抗拉强度分别为640,970 MPa,伸长率为52.2%,断面收缩率为67.5%,20 ℃和-40 ℃下的冲击吸收功平均值分别为311,280 J,疲劳极限为330 MPa,耐腐蚀性能优于316L不锈钢的;试验钢对缺口不敏感,可以随较大偏斜力;该高氮奥氏体不锈钢的性能完全满足海洋工程紧固件的要求,并优于通用的海洋工程紧固件用钢的。
标    签 高氮奥氏体不锈钢   紧固件   海洋工程   力学性能   耐腐蚀性   high nitrogen austenite stainless steel   fastener   marine engineering   mechanical property   corrosion resistance  
 
Abstract
A kind of high nitrogen austenite stainless steel 0Cr20Mn18N0.8 was newly developed. The properties such as static tension, notch tension, deflected tension, impact, fatigue and anti-corrosion were studied and compared with those of 316L stainless steel. The feasibility of the steel for the marine engineering fasteners was also analyzed. The results show that the yield strength and tensile strength under static tension was 640, 970 MPa, respectively, with the elongation of 52.2% and the reduction in area of 67.5%. The average impact toughness at 20℃ and -40℃ was 311, 280 J, respectively, and the fatigue limit was 330 MPa. The corrosion resistance was better than that of 316L stainless steel. The tested steel was not sensitive to the notch and can bear a relatively large deflected force. The performance of the high nitrogen austenite stainless steel completely met the requirements of the marine engineering fasteners and was better than those of commonly used marine engineering steels for fasteners.

中图分类号 TG142.71   DOI 10.11973/jxgccl201708016

 
  中国光学期刊网论文下载说明


所属栏目 材料性能及应用

基金项目 总装装备预研基金资助项目(9140A18050114BQ02259)

收稿日期 2016/7/28

修改稿日期 2017/7/7

网络出版日期

作者单位点击查看

备注高鹏(1992-),男,山西长治人,硕士研究生

引用该论文: GAO Peng,HE Meng,CAI Baofang,ZHOU Qi,WANG Kehong,PENG Yong,KONG Jian. Property of 0Cr20Mn18N0.8 High Nitrogen Austenite Stainless Steel for Marine Engineering Fasteners[J]. Materials for mechancial engineering, 2017, 41(8): 70~74
高鹏,贺蒙,蔡葆昉,周琦,王克鸿,彭勇,孔见. 海洋工程紧固件用0Cr20Mn18N0.8高氮奥氏体不锈钢的性能[J]. 机械工程材料, 2017, 41(8): 70~74


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】LV W Y, PAN C, SU W,et al. A study on atmospheric corrosion of 304 stainless steel in a simulated marine atmosphere[J]. Journal of Materials Engineering and Performance, 2015, 24(7):2597-2604.
 
【2】彭世丹. 冷镦钢SCM435质量分析及轧制工艺试验研究[D]. 沈阳:东北大学, 2008.
 
【3】祖荣祥. 高强度螺栓钢的开发与应用[J].特殊钢,1995(5):1-7.
 
【4】张海军, 胡卫东, 刘宝安,等. 达克罗涂层防腐技术及应用[J]. 电镀与精饰, 2013, 35(7):24-28.
 
【5】PEPI M. Caution is advised when specifying stainless steel fasteners[J]. Journal of Failure Analysis and Prevention, 2005, 5(1):72-78.
 
【6】梁剑雄, 刘振宝, 杨志勇. 高强不锈钢的发展与应用技术[J]. 宇航材料工艺, 2013, 43(3):1-11.
 
【7】SVYAZHIN A G, SIWKA J, KAPUTKINA L M. High-nitrogen steels:The current state and development trends[M]//Advanced Steels. Heidelberg:Springer Berlin Heidelberg, 2011:368.
 
【8】SUMITA M, HANAWA T, TEOH S H. Development of nitrogen-containing nickel-free austenitic stainless steels for metallic biomaterials-Review[J]. Materials Science & Engineering C, 2004, 24(6/7/8):753-760.
 
【9】XIANG B, ZHANG J, DUAN J Z,et al. Study on corrosion of steels in marine environment by corrosion simulation device[J]. Materials and Corrosion, 2003, 54(9):697-702.
 
【10】杨振国, 张继明, 李守新,等. 42CrMoVNb细晶高强钢的疲劳行为[J]. 金属学报, 2004, 40(4):367-372.
 
【11】RAVIERS J, SLAVENS G. Strengthening characteristics of nitrogen-alloyed 201 stainless steel[J]. Journal of Materials Engineering and Performance, 1995, 4(6):697-708.
 
【12】夏德贵. 0Cr17Ni4Cu4Nb马氏体沉淀硬化不锈钢耐海水腐蚀性能研究[D]. 哈尔滨:哈尔滨工程大学, 2007.
 
【13】MISIEK T, KÄPPLEIN S, ULBRICH D. Selecting materials for fastening screws for metal members and sheeting[J]. Steel Construction. 2013,6(1),39-46.
 
【14】柴武倩,杨强云,杨川,等.汽车张紧轮紧固螺栓断裂分析[J]. 机械工程材料,2015,39(5):103-110.
 
【15】孙浩然. 汽车紧固件用钢的发展动向[J]. 中国冶金, 2011, 21(7):7-9.
 
【16】WU W, HAO W K, LIU Z Y,et al. Corrosion behavior of E690 high-strength steel in alternating wet-dry marine environment with different pH values[J]. Journal of Materials Engineering and Performance, 2015, 24(12):4636-4646.
 
【17】郑少华. 表面复合处理工艺对合金钢紧固件力学性能和抗腐蚀性能的影响[D]. 成都:西南交通大学, 2014.
 
相关信息
   标题 相关频次
 紧固件力学性能试验夹具
 4
 氮含量对29Cr铸造超级双相不锈钢深冷组织和性能的影响
 3
 铬含量对00Cr25Ni7Mo3N双相不锈钢力学性能及耐腐蚀性能的影响
 3
 硅对铁基合金组织和耐蚀性能的影响
 3
 热处理对Ni-Ga-Fe系铁磁形状记忆合金力学及耐蚀性能的影响
 3
 热挤压对铸态Mg-3.5Al-3.5Ca-0.6Mn合金组织与性能的影响
 3
 热浸镀Al-43%Zn-1.6%Si合金新工艺及其镀层的组织和性能
 3
 深度冷旋对超薄壁大径厚比镍基合金焊接筒性能的影响
 3
 深海油气输送用X70厚壁直缝埋弧焊钢管的耐蚀性
 3
 深冷时间对2906超级双相不锈铸钢组织及性能的影响
 3
 钛含量对低镍铜合金显微组织和性能的影响
 3
 碳含量对FeCoCrNiMnCx高熵合金显微组织与性能的影响
 3
 钨含量对新型高铬锰氮双相不锈钢Cr29Mn12Ni2N0.6Wx组织和性能的影响
 3
 稀土钇含量对B10铜合金组织和性能的影响
 3
 医疗器械用高氮不锈钢中厚板钨极氩弧焊接接头的组织与性能
 3
 1.25Cr0.5MoSi钢的焊接工艺评定
 2
 1060工业纯铝累积叠轧后的力学性能
 2
 1060铝在累积轧制中组织和性能的演变
 2
 10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能
 2
 12Cr13钢预热处理工艺参数优化
 2
 14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能
 2
 15Ni3CrMoV与10Ni5CrMoV异种钢对接接头的显微组织及力学性能
 2
 16Mo3钢大直径大变形量试制中频弯管的组织与性能
 2
 17-4PH不锈钢表面TiO2膜及其多层膜的结构与性能
 2
 2 000 t水压机立柱断裂分析
 2
 2024铝合金电子束焊接接头的显微组织与力学性能
 2
 20Cr钢与B级钢焊接接头的组织和性能
 2
 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能
 2
 22Mn2SiVBS热轧无缝钢管控冷时的组织与性能
 2
 240 MPa级高强IF钢的冷轧压下率和退火温度
 2