某汽油加氢脱硫装置引风机系统腐蚀原因及处置措施
          
Corrosion Reasons and Corresponding Protective Measures of Suction Fan System in a Gasoline Hydrodesulfurization Unit

摘    要
通过对汽油加氢脱硫装置加热炉引风机系统腐蚀产物的现场目测、操作条件和介质组成的考察,探讨了该系统的腐蚀原因。结果表明: 汽油加氢脱硫装置加热炉引风机系统腐蚀的原因是烟气中的硫化物在低温条件下形成的露点腐蚀,并对此具体问题提出了相应的防护措施。
标    签 汽油加氢脱硫   引风机   低温露点腐蚀   防护措施   gasoline hydrodesulfurization   induced draft fan   low temperature dew point corrosion   protective measures  
 
Abstract
The corrosion reasons for the induced draft fan system of heating furnace in a gasoline hydro-desulfurization unit were studied through on-site observation of the corrosion products and investigation of operating conditions and medium composition. The results show that dew point corrosion of sulfur compounds in flue gas at low temperature was the main reason for system corrosion. And some corresponding protective measures were propounded to solve this problem.

中图分类号 TG172   DOI 10.11973/fsyfh-201612016

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 失效分析

基金项目

收稿日期 2015/7/1

修改稿日期

网络出版日期

作者单位点击查看


备注陶武军(1982-),工程师, 学士,从事炼化设备日常维护技术管理、炼油设备腐蚀防护技术管理的相关研究工作

引用该论文: TAO Wu-jun,QI Yao-guang,ZOU An. Corrosion Reasons and Corresponding Protective Measures of Suction Fan System in a Gasoline Hydrodesulfurization Unit[J]. Corrosion & Protection, 2016, 37(12): 1023


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】张德印,张扬. 石化企业火焰加热炉腐蚀及防护措施[J]. 石油化工腐蚀与防护,2005,22(3): 25-29.
 
【2】姚庆. 工艺加热炉腐蚀原因分析与对策[J]. 腐蚀与防护,2006,27(2): 77-79.
 
【3】李德付. 关于燃气加热炉低温腐蚀的原因与对策[J]. 现代化工,2006,26(1): 59-61.
 
相关信息
   标题 相关频次
 电网铜材在含H2S大气中的腐蚀研究现状
 1
 接地系统对区域阴极保护影响规律及解决措施研究现状
 1
 金属在固液两相流体中的冲刷腐蚀及其防护
 1
 强电线路下的阴极保护管道交流干扰防护措施
 1
 输电线路公共走廊内管道上感应的交流电危害及防护
 1
 苏南成品油管道交流杂散电流干扰检测及防护措施
 1
 提高海洋环境钢筋混凝土构筑物耐久性措施综述
 1
 卫58块油井结垢腐蚀因素分析及防护措施
 1
 雅克拉-大涝坝凝析气田井下油管腐蚀分析
 1
 雅克拉凝析气田采油树构件腐蚀分析与防护措施
 1
 中原油田柳屯至文留输气管线腐蚀调查
 1