接地材料对埋地金属管道阴极保护效果及电流需求量的影响
          
Effect of Electrical Grounding Material on the Cathodic Protection of Buried Metallic Pipeline and Its Current Demand

摘    要
通过室内模拟试验探讨了接地材料的极化特性及其对管道阴极保护电流需求量的影响,同时也研究接地极与管道的间距对管道极化电位的影响。结果表明: 接地材料为接地模块、铜包钢、锌包钢时,体系对阴极保护电流的需求量依次降低,锌包钢作为接地材料的服役性能更优越。当接地极与试片的间距超过试样直径的5倍时,对试样极化电位基本不变,即对试样极化电位的影响可以忽略。
标    签 区域性阴极保护   接地   管道   阴极保护效果   regional cathodic protection   grounding   pipeline   efficiency of cathodic protection  
 
Abstract
Polarization characteristics of various grounding materials were measured in laboratory and then the effect of grounding materials on cathodic protection current demand of pipeline was discussed. Moreover, the effect of space between grounding and pipeline on polarization potential was studied by indoor simulation experiments. The results indicated that cathodic protection current demand decreased in turn, when the grounding material was grounding module, copper clad steel and zinc clad steel. Among them, the zinc clad steel was the best material for grounding. When the space between grounding and pipeline was beyond 5 times of sample diameter, the polarization potential of sample stayed stable, indicating that the effect of space was negligible.

中图分类号 TE832   DOI 10.11973/fsyfh-201612012

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 应用技术

基金项目

收稿日期 2015/6/15

修改稿日期

网络出版日期

作者单位点击查看


备注杜艳霞(1980-),博士,副研究员,从事腐蚀与防护研究工作

引用该论文: JIANG Zi-tao,DU Yan-xia,LIANG Yi,XIONG Jin-gen,SUN Bing-bing. Effect of Electrical Grounding Material on the Cathodic Protection of Buried Metallic Pipeline and Its Current Demand[J]. Corrosion & Protection, 2016, 37(12): 1003


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】KIRKPATRICK E L. Electrical grounding and cathodic protection issues in large generating stations[J]. Material Performance,2001,40(11):17-19.
 
【2】马伟平,张国忠,白宗成,等. 区域性阴极保护技术研究进展[J]. 油气储运,2005,24(9):38-42.
 
【3】罗卫国,赵新伟,白真权,等. 阿赛输油管线腐蚀状况调查及分析[J]. 焊管,2004,27(3):14-17.
 
【4】杜艳霞,张国忠. 输油泵站区域性阴极保护实施中的问题[J]. 腐蚀与防护,2006,27(8):417-421.
 
【5】KIRKPATRICK E L. Electrical grounding case histories[C]//Corrosion 2003. Houston,Texas:NACE,2003:701.
 
【6】KIRKPATRICK E L. Alternatives to copper grounding in sites requiring cathodic protection[C]//Corrosion 1986. Houston,Texas:NACE,1986:9.
 
【7】葛艾天,刘权,陈国桥. 铜接地系统对输油气站场埋地管道影响[J]. 天然气与石油,2010,28(2):15-17.
 
【8】ROMANOFF M,SPELLER F N. Underground Corrosion[M]. Washington:US Government Printing Office,1957.
 
【9】HUSOCK B. The effect of electrical grounding systems on underground corrosion and cathodic protection[J]. American Institute of Electrical Engineers,1960,79(1):5-10.
 
【10】KIRKPATRICK E L. Effects of electrical grounding on corrosion[C]//Corrosion 1979. Houston,Texas:NACE,1979:53.
 
【11】BLADHOLM E F,KORMENDy L J. Cathodic protection and isolation solve corrosion problem of subsurface piping in generating station[J]. Material Performance,1963,2(2):2-27.
 
【12】GHESQUIERE J D. Cathodic protection and zinc grounding in industrial plant construction[J]. Corrosion,1961,17(3):149-153.
 
【13】闫爱军,陈沂,冯拉俊. 几种接地网材料在土壤中的腐蚀特性研究[J]. 腐蚀科学与防护技术,2010,22(3):197-199.
 
【14】聂新辉,郑敏聪,李建华. 铜质接地网材料电化学腐蚀行为[J]. 腐蚀与防护,2012,33(9):817-819.
 
【15】GUMMOW R A. Cathodic protection current requirements for electrical grounding materials[C]//Corrosion 2004. Houston,Texas:NACE,2004:45.
 
相关信息
   标题 相关频次
 接地系统对区域阴极保护影响规律及解决措施研究现状
 5
 交流干扰对埋地管线阴极保护的影响
 4
 胶日线天然气管道交流干扰评估与缓解
 4
 廉溪大道并行天然气管道腐蚀风险检测与分析
 4
 埋地管道交流干扰缓解效果影响因素
 4
 输油泵站区域性阴极保护实施中的问题
 4
 四种交流排流器服役性能对比
 4
 油气管道阴极保护阳极干扰检测与分析
 4
 长输油气管道工艺站场的区域性阴极保护
 3
 pH稳定剂抑制管道潮湿CO2腐蚀的研究进展
 2
 X70管线钢在醋HAc-CO2共存环境中的顶部腐蚀行为
 2
 X80钢在新疆不同土壤环境中的氢脆行为
 2
 阿拉斯加冻土区管道阴极保护技术
 2
 北京燃气管道牺牲阳极服役参数测试及变化规律
 2
 沉积砂对X60钢在饱和CO2油田水中腐蚀行为的影响
 2
 大口径管道远场涡流缺陷检测仿真建模
 2
 大数据时代油气管道的安全与防护
 2
 导管架牺牲阳极阴极保护数值模拟评价与优化改造
 2
 点腐蚀损伤管道剩余强度的评价方法
 2
 电力接地网用铜铝伪合金涂层材料
 2
 电气化铁路对长输管道的交流干扰及防护
 2
 电子显微分析仪器稳定运行的环境因素分析与对策
 2
 动态直流杂散电流干扰下埋地管道的腐蚀行为
 2
 防冻型参比电极在冻土区阴极保护系统上的应用
 2
 非接触式磁致伸缩导波管道无损检测系统的研制
 2
 分离式励磁结构对管道腐蚀缺陷漏磁场的影响
 2
 干耦合式磁致伸缩导波管道检测系统
 2
 钢制管道外防腐蚀涂料的应用进展
 2
 工业管道无损检测技术
 2
 构件形状对金属磁记忆检测的影响
 2