环氧防锈漆在3种腐蚀环境中的电化学行为
          
Electrochemical Behaviors of Epoxy Coatings in 3 Kinds of Corrosion Environments

摘    要
采用电化学阻抗谱(EIS)技术研究了环氧防锈漆经实海浸泡试验和质量分数3.5% NaCl溶液浸泡试验、盐雾试验2种实验室模拟试验后的电化学行为,测量了涂层试样在3种腐蚀环境中0.01 Hz低频阻抗(|Z|0.01 Hz),探究了实海浸泡试验和两种实验室模拟试验的相关性。结果表明: |Z|0.01 Hz在3种试验环境中的变化趋势相同,实海浸泡试验和2种实验室模拟试验的试验结果具有很好的相关性; 3种试验环境对涂层破坏作用由小到大依次为: 3.5% NaCl溶液浸泡试验<实海浸泡试验<盐雾试验。
标    签 电化学阻抗谱   低频   环氧涂层   electochemical impedance spectroscopy   low frequency   epoxy coating  
 
Abstract
Electrochemical behaviors of an epoxy coating in real sea immersion test, 3.5% (mass) NaCl solution immersion test and salt spray test were studied by electrochemical impedance spectroscopy ( EIS). Coating impedance in low frequency of 0.01 Hz (|Z|0.01 Hz) were tested in the 3 kinds of corrosion environments, and the relationships between real sea immersion test and 2 types of laboratory experiments were also analyzed. The results indicated that the trends of |Z|0.01 Hz in 3 kinds of corrosion environments were similar. The results from real sea immersion test and 2 types of laboratory experiments were correlated well, and the order of the damaging effect of the three corrosive environments on coating was as follows: 3.5% NaCl solution < seawater immersion experiment < salt spray.

中图分类号 TG174.4   DOI 10.11973/fsyfh-201612007

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2015/7/16

修改稿日期

网络出版日期

作者单位点击查看


备注张寒露(1980-),工程师,硕士,从事材料的腐蚀与防护研究

引用该论文: ZHANG Han-lu,CAO Jing-yi,DUN Yu-chao,TANG Yu-ming,ZUO Yu. Electrochemical Behaviors of Epoxy Coatings in 3 Kinds of Corrosion Environments[J]. Corrosion & Protection, 2016, 37(12): 979


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】牟献良,田月娥,汪学华. 碳钢和低合金钢模拟加速试验与大气腐蚀试验的相关性[J]. 环境技术,2001,19(4):14-17.
 
【2】王绍明. 模拟大气环境加速腐蚀试验的研究[J]. 装备环境工程,2005,2(4):65-68.
 
【3】郝美丽,曹学军,封先河,等. 铝合金室内加速腐蚀与大气暴露腐蚀的相关性[J]. 兵器材料科学与工程,2006,29(5):28-31.
 
【4】王晶晶,董士刚,叶美琪,等. 环氧涂层室外暴晒和室内加速老化试验相关性研究[J]. 表面技术,2006,35(1):36-39.
 
【5】ZUO Y,PANG R,LI W,et al. The evaluation of coating performance by the variations of phase angles in middle and high frequency domains of EIS[J]. Corrosion Science,2008,50(12):3322-3328.
 
【6】张鉴清,曹楚南. 电化学阻抗谱方法研究评价有机涂层[J]. 腐蚀与防护,1998,19(3):99-104.
 
【7】MCINTYRE J M,PHAM H Q. Electrochemical impedance spectroscopy:a tool for organic coatings optimizations[J]. Progress in Organic Coatings,1996,27(1):201-207.
 
【8】DEFLORIAN F,FEDRIZZI L,ROSSI S,et al. Organic coating capacitance measurement by EIS:ideal and actual trends[J]. Electrochimica Acta,1999,44(24):4243-4249.
 
【9】AMIRUDIN A,THIENY D. Application of electrochemical impedance spectroscopy to study the degradation of polymer-coated metals[J]. Progress in Organic Coatings,1995,26(1):1-28.
 
【10】MARCHEBOIS H,KEDDAM M,SAVALL C,et al. Zinc-rich powder coatings characterisation in artificial sea water[J]. Electrochimica Acta,2004,49(11):1719-1729.
 
【11】XIE D,JIMING H U,TONG S,et al. Influence of zinc content and surface contamination on the electrochemical behaviors of epoxy zinc-rich primer[J]. Acta Metallurgica Sinica-Chinese Edition,2004,40(1):103-108.
 
【12】MAHDAVIAN M,ATTAR M M. Another approach in analysis of paint coatings with EIS measurement:Phase angle at high frequencies[J]. Corrosion Science,2006,48(12):4152-4157.
 
相关信息
   标题 相关频次
 富镁涂层对LY12铝合金点蚀的抑制作用
 4
 环氧厚涂底漆在干湿交替环境条件下的劣化过程
 4
 环氧涂层中锌铬黄颜料对镁合金的防蚀机理
 4
 镍钛合金在磷酸盐缓冲溶液中的亚稳态点蚀行为
 4
 载荷对砂浆中碳钢腐蚀的影响
 4
 表面电镀钯膜的316L不锈钢在高温稀硫酸/硫酸盐溶液中的耐蚀性
 3
 氯离子浓度和温度对Cr3钢CO2/H2S腐蚀的影响
 3
 咪唑啉季铵盐对A3碳钢在NaNO2+NaCl溶液中点蚀行为的影响
 3
 AP1000核电站CA01结构模块的环氧涂层缺陷
 2
 Cr13钢在含饱和CO2介质中腐蚀的影响因素
 2
 表面机械处理对5083铝合金表面形貌和拉伸性能的影响
 2
 海洋环境蒙脱土改性聚苯胺环氧涂层的防腐蚀性能
 2
 含宏观孔通孔多孔铝的低频阻尼行为
 2
 聚苯胺对环氧涂层防腐蚀性能的影响
 2
 铝合金阳极氧化膜醋酸镍封闭方法耐蚀性研究
 2
 纳米SiO2改性环氧涂层海洋腐蚀规律
 2
 新型环氧涂层在油水井套管上应用的评价试验
 2
 09Cr2AlMoRE钢和N80油套管钢的CO2腐蚀电化学行为
 1
 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验
 1
 1050A铝合金在模拟海洋大气环境中周浸腐蚀行为
 1
 15Cr低合金钢和N80钢的二氧化碳腐蚀性能对比
 1
 16Mn钢在管输俄罗斯原油析出水中的腐蚀行为
 1
 20#钢在三元复合驱弱碱体系采出液中的腐蚀与防护
 1
 200 ℃回火对X80管线钢在NaHCO3溶液中电化学腐蚀的影响
 1
 2197铝锂合金在不同热处理状态下的晶间腐蚀及剥蚀行为
 1
 304L不锈钢在硼酸水溶液中的腐蚀行为
 1
 7A04-T6铝合金中金属间化合物对其阳极氧化膜耐蚀性的影响
 1
 Alodine 1200S化学转化处理时间对新型2198铝锂合金耐蚀性能的影响
 1
 C12-6-C12型Gemini阳离子表面活性剂缓蚀性能与行为的研究
 1
 Cl-浓度对2A12铝合金电化学行为的影响
 1