镀锌层表面钝化膜在5% NaCl溶液中的腐蚀降解过程和半导体行为
          
Corrosion Degradation Process and Semiconducting Behavior of Passivation Film on Zinc Coating in 5% NaCl Solution

摘    要
采用扫描电化学显微镜(SECM)分析技术、电化学阻抗谱(EIS)和电容-电位测试研究了镀锌层表面钝化膜在质量分数5% NaCl溶液中的腐蚀降解过程和半导体行为。结果表明: 浸泡过程中随着水和离子逐渐侵入钝化膜,钝化膜发生着缓慢的腐蚀降解,钝化膜在浸泡初期保持稳定,能够对基体金属起到较好的保护作用; 钝化膜表现出n型半导体特征,随着浸泡时间的延长,Mott-Schottky曲线拟合直线的斜率逐渐减小,钝化膜载流子密度逐渐增大,表明钝化膜在浸泡过程中发生缓慢的腐蚀降解。
标    签 扫描电化学显微镜   钝化膜   腐蚀降解   Mott-Schottky曲线   scanning electrochemical microscopy (SECM)   passivation film   corrosion degradation   Mott-Schottky curve  
 
Abstract
The corrosion degradation process and semiconducting character of passivation film on the surface of zinc coating were examined in 5% (mass) NaCl solution by means of scanning electrochemical microscopy (SECM), electrochemical impedance spectroscopy (EIS) and potential-capacitance measurement. The results show that as water and ions gradually invaded into the coating, the passivation film was under slow corrosion degradation. The passivation film kept stable and provided good protection for substrate during the early immersion in corrosion electrolyte. The passivation film showed the characteristics of n-type semiconductor. With the increase of immersion time, the slope of Mott-Schottky curves dropped and the carrier density rose, reflecting that the passivation film was under slow corrosion degradation in immersion process.

中图分类号 TG174.4   DOI 10.11973/fsyfh-201612006

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目 南通市产学研协同创新项目(BC201410)

收稿日期 2015/8/16

修改稿日期

网络出版日期

作者单位点击查看


备注钟庆东(1969 - ), 教授,博士

引用该论文: ZHANG Jun-liang,ZHAO Qi-liang,ZHONG Qing-dong,GUO Wei. Corrosion Degradation Process and Semiconducting Behavior of Passivation Film on Zinc Coating in 5% NaCl Solution[J]. Corrosion & Protection, 2016, 37(12): 973


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】孙秋霞,张鉴清,林昌健. 阻抗谱定量分析金属/有机涂层界面粘接力[J]. 物理化学学报,2005,20(11):1297-1302.
 
【2】雷彤,赵孔双. 导电高分子膜的电化学阻抗谱研究进展[J]. 化学通报,2001,64(1):11-11.
 
【3】MONTEMOR M F,FERREIRA M G S. Cerium salt activated nanoparticles as fillers for silane films: evaluation of the corrosion inhibition performance on galvanised steel substrates[J]. Electrochimica Acta,2007,52(24):6976-6987.
 
【4】MONTEMOR M F,FERREIRA M G S. Analytical characterization of silane films modified with cerium activated nanoparticles and its relation with the corrosion protection of galvanised steel substrates[J]. Progress in Organic Coatings,2008,63(3):330-337.
 
【5】卢琳,李晓刚,高瑾. 有机涂层/金属界面腐蚀的微区电化学[J]. 化学进展,2011,23(8):1618-1626.
 
【6】骆鸿,魏丹,董超芳,等. 金属腐蚀微区电化学研究进展(1)扫描电化学显微镜技术[J]. 腐蚀与防护,2009,30(7):437-441.
 
【7】卢小泉,王晓强,胡丽娜. 扫描电化学显微镜及其在界面电化学研究中的应用[J]. 化学通报,2004,67(9):673-678.
 
【8】曹发和,夏妍,刘文娟,等. SECM基本原理及其在金属腐蚀中的应用[J]. 电化学,2013(5): 393-401.
 
【9】SOUTO R M,GONZLEZ-GARCA Y,GONZLEZ S. Evaluation of the corrosion performance of coil-coated steel sheet as studied by scanning electrochemical microscopy[J]. Corrosion Science,2008,50(6):1637-1643.
 
【10】BASTOS A C,SIM01ES A M. Application of the scanning electrochemical microscope to the examination of organic coatings on metallic substrates[J]. Progress in Organic Coatings,2005,53(3):177-182.
 
【11】HAMADA T,NOMURA H. Direct current resistivi-ty of degraded organic film for pre-coat metal[J].Progress in Organic Coatings,1999,37(3):141-148.
 
【12】王超,钟庆东,周国治,等. 环氧树脂/碳钢电极在硫酸溶液中的半导体导电行为[J]. 物理化学学报,2008,24(7):1277-1282.
 
【13】王超,盛敏奇,钟庆东,等. 碳钢/醇酸涂层在5% NaCl溶液中的极化及半导体行为[J]. 化学学报,2009,67(8):709-715.
 
【14】SOUTO R M,GONZLEZ-GARCA Y,IZQUIERDO J,et al. Examination of organic coatings on metallic substrates by scanning electrochemical microscopy in feedback mode:revealing the early stages of coating breakdown in corrosive environments[J]. Corrosion Science,2010,52(3):748-753.
 
【15】GU J F,ZHANG J L,ZHONG Q D,et al. Evaluation of corrosion resistance of silane film modified with SiO2 nano-particles on zinc coatings[C]//Intermational Conference on Material Engineering and Application.\[S.l.\]:\[s.n.\],2015.
 
【16】PETERSON M W,PARKINSON B A. Photoelectrochemical investigation of several II-IV-V/sub 2/semiconducting glasses[J]. J Electrochem Soc (United States),1986,133(12).
 
【17】CHENG Y F,LUO J L. A comparison of the pitting susceptibility and semiconducting properties of the passive films on carbon steel in chromate and bicarbonate solutions[J]. Applied Surface Science,2000,167(1):113-121.
 
【18】ALVES V A,BRETT C M A. Characterisation of passive films formed on mild steels in bicarbonate solution by EIS[J]. Electrochimica Acta,2002,47(13):2081-2091.
 
相关信息
   标题 相关频次
 镀锌钢板硅烷钝化膜的制备及其电化学性能
 8
 硼酸缓冲溶液pH对黄铜表面钝化膜电化学性能的影响
 4
 H2S/CO2腐蚀环境中镍基合金825表面钝化膜的电化学特性
 3
 pH对316L不锈钢电化学性能的影响
 3
 晶粒度与介质中Cl-浓度对铜表面钝化膜的影响
 3
 304不锈钢在RCC-M1310标准下的耐蚀性
 2
 AISI304不锈钢钝化膜在电解质溶液中腐蚀时的半导体性质
 2
 Fe-Me(Me=Co,Ni,Co-Ni)合金化层表面钝化膜的电化学行为
 2
 t8/5对高强度余热处理棒材焊接热影响区组织和力学性能的影响
 2
 超声波作用下电沉积纳米晶Co-W合金镀层
 2
 臭氧与Ni2+对碳钢表面磷化的影响
 2
 低碳钢表面Fe-Co合金层的热扩渗制备及腐蚀电化学行为
 2
 镀锌墨绿色钝化膜的制备与表征
 2
 复合电沉积的电化学测试方法与研究进展
 2
 钢筋钝化膜半导体性能的Mott-Schottky研究
 2
 基于正交试验设计与人工神经网络优化镀铬工艺
 2
 晶粒度对铜点蚀行为的影响
 2
 晶粒度对一些常用金属耐腐蚀性能的影响
 2
 卷材涂料研究进展
 2
 冷凝液pH对消声器用409不锈钢腐蚀行为的影响
 2
 硫脲对HR-2不锈钢的缓蚀性
 2
 纳米Fe3O4-K2O·3Al2O3·6SiO2·2H2O 金色亮粉复合颗粒改性环氧涂层用于H68黄铜涂层的耐蚀性
 2
 纳米SiO2对低碳钢表面常温磷化处理的影响
 2
 纳米石墨对无氰电刷镀银镀层性能的影响
 2
 汽车大梁用BS700MC低碳微合金钢焊接接头的组织和力学性能
 2
 酸性环境中pH对低碳钢表面Ni-Mn合金沉积层的影响
 2
 酸性硫酸盐电解液中沉积Ni-W合金的动力学
 2
 碳钢及环氧清漆在不同溶液中的半导体导电行为
 2
 温度对316L不锈钢在硼酸溶液中腐蚀电化学行为的影响
 2
 有机清漆在5%氢氧化钠溶液中的半导体导电行为
 2