冷轧IF钢板表面状态对磷化膜质量的影响
          
Effects of Surface Property of Cold Rolled IF Steel Sheets on Phosphate Coating Quality

摘    要
利用扫描电镜(SEM)、X射线光电子能谱(XPS)和电化学测试等方法研究了冷轧IF钢板表面状态对其磷化膜质量的影响。结果表明: 表面夹杂物及析出相对冷轧IF钢板表面磷化膜具有明显影响; 通过铸坯机清处理以及降低板坯加热温度,可降低冷轧IF钢板表面夹杂物及析出相含量,有效控制有害元素在表面的富集,有利于提高钢板表面均匀性,控制冷轧板材表面活性,从而改善磷化膜质量,并提高磷化膜致密性及耐蚀性。
标    签 冷轧板   表面元素   夹杂物   析出相   磷化膜   cold rolled steel   surface element   inclusion   precipitated phase   phosphate coating  
 
Abstract
Scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and electrochemical testing were utilized to investigate the effect of the surface property of cold rolled IF steel sheets on the quality of phosphate coating. The results show that inclusions and precipitated phases played an important role in the phosphate coating of the cold rolled IF steel sheets. The flame cleaning and decreasing the slab heating temperature were the effective ways to reduce inclusions and precipitated phases and control the enrichment of harmful elements on the steel surface. As a result, the homogeneity of the steel surface increased as well as the surface activity, which was conducive to improve the density and the corrosion resistance of the phosphate coating.

中图分类号 TG178   DOI 10.11973/fsyfh-201612004

 
  购买该论文  中国光学期刊网论文下载说明


所属栏目 试验研究

基金项目

收稿日期 2015/8/2

修改稿日期

网络出版日期

作者单位点击查看

联系人作者生海(shmeer@126.com)

备注生 海(1984-),高级工程师,博士,从事汽车板涂装及耐腐蚀技术研究

引用该论文: SHENG Hai,YANG Jian-wei,CAO Jian-ping,XU Jing,GAO Li-jun,LIU Li-wei. Effects of Surface Property of Cold Rolled IF Steel Sheets on Phosphate Coating Quality[J]. Corrosion & Protection, 2016, 37(12): 966


论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
分享到新浪微博 分享到腾讯微博 分享到人人网 分享到 Google Reader 分享到百度搜藏分享到Twitter

参考文献
【1】陈义庆,徐小连,李天统,等. 表面粗糙度对冷轧钢板磷化质量的影响[J]. 腐蚀与防护,2011,32(9):697-700.
 
【2】PETSCHEL M. Pollution prevention and conversion coating in the automobile industry[J]. Metal Finishing,1996,94(9):26-29.
 
【3】郝晓东,刘昕,张建,等. 冷轧板表面粗糙度对磷化性能的影响[J]. 腐蚀与防护,2014,35(4):387-389.
 
【4】CVIJOVIC I,PAREZANOVIC I,SPIEGEL M. Influence of H2-N2 atmosphere composition and annealing duration on the selective surface oxidation of low-carbon steels[J]. Corrosion Science,2006,48(4):980-993.
 
【5】田亚强,吴健,魏英立,等. 罩式退火冷轧家电板的耐腐蚀性能及腐蚀机理[J]. 机械工程材料,2014,39(5):33-36.
 
【6】周剑丰,张波. RH-MFB生产过程对夹杂物的影响分析[J]. 炼钢,2012,28(3):27-32.
 
【7】郑万任,胡勤东,李凯玉. 降低超低碳钢冷轧产品夹杂的生产控制实践[J]. 山东冶金,2012,34(5):22-24.
 
【8】马衍伟,王先进. 超深冲IF钢研究的最新进展[J]. 钢铁,1998,33(4):1-8.
 
【9】GUO L Q,ZHAO X M,WANG B C,et al. The initial stage of atmospheric corrosion on interstitial free steel investigated by in situ SPM[J]. Corrosion Science,2013,70:188-193.
 
【10】唐复平,常桂华,栗红,等. 超低碳钢钢中夹杂物的研究[J]. 钢铁,2007,42(1):20-22.
 
【11】黄健,闵义,姜茂发,等. IF钢生产过程非金属夹杂物的演变行为[J]. 东北大学学报(自然科学版),2013,34(3):368-372.
 
相关信息
   标题 相关频次
 0Cr13铁素体不锈钢丝在模压过程中开裂的原因
 2
 0Cr18Ni9不锈钢热轧卷分层原因分析
 2
 1000MW超超临界机组C12A堵板阀裂纹成因分析
 2
 13Cr钢防砂工具转换接头开裂原因分析
 2
 2.25Cr1Mo钢中的夹杂物和晶粒度
 2
 2.25CrMoV钢于夹杂物和晶界处开裂低周疲劳裂纹扩展的原位观测
 2
 20CrMnTi齿轮钢铸坯缺陷引起的开裂分析
 2
 304不锈钢表面锈蚀原因分析
 2
 37Mn5钢管内壁起皮原因分析
 2
 40Cr钢汽车半轴断裂原因分析
 2
 45钢棒料冲击功偏低的原因分析
 2
 5083铝合金支架开裂失效分析
 2
 55CrSi钢气门弹簧断裂原因分析
 2
 70 mm厚度Q345E钢板低温冲击吸收功不合格原因分析
 2
 7150铝合金在热压缩变形过程中的动态组织演变
 2
 718H钢与40Cr13钢中心疏松的原因分析及改进措施
 2
 B7螺杆上的螺纹剥落原因分析
 2
 BM510汽车大梁钢冷弯开裂原因分析
 2
 K418高温合金涡轮裂纹产生原因分析
 2
 La-Ce对X70管线钢耐蚀性能的影响
 2
 NIV型平列双扭弹簧延迟断裂分析
 2
 PH13-8Mo高强不锈钢在不同温度时效后的析出相及其对力学性能的影响
 2
 Q195钢盘条折弯开裂原因分析
 2
 Q235B钢热轧板带孔洞缺陷的形成原因
 2
 Q235钢板表面裂纹形成原因分析
 2
 Q345B钢板拉伸性能不合格原因分析
 2
 Q345R钢板断后伸长率不合格原因分析
 2
 Q460C钢板力学性能不合格原因分析
 2
 SA-210C钢管扩口裂纹的产生原因分析
 2
 T91钢在650 ℃时效过程中析出相的变化
 2